Foamed polypropylene composition

ABSTRACT

The present invention is directed to a polypropylene composition (C) comprising a heterophasic propylene copolymer and an inorganic filler, the use of said polypropylene composition (C) for the production of a foamed article and a foamed article obtained from said polypropylene composition (C).

The present invention is directed to a polypropylene composition (C) comprising a heterophasic propylene copolymer and an inorganic filler, the use of said polypropylene composition (C) for the production of a foamed article and a foamed article obtained from said polypropylene composition (C).

Plastic materials featured by a reduced weight with preservation of the mechanical property profile are gaining more and more interest in the automotive industry since the European Union has approved tough CO₂ limits which mandate the car manufacturer to cut emission from current 160 g/km to 120 g/km or below. Thus, there is a need for weight saving concepts in order to fulfil said legislation.

The foam injection-moulding (FIM) technology can be used to produce low-density parts. It can be applied for visible and non-visible automotive parts. Foamed parts have the advantage of reduced density, low shrinkage and warpage, but the mechanical properties and surface appearance of the parts are poor whereupon the majority of foamed parts are not used for visible interior or exterior applications.

Accordingly, there is a need in the art for a polypropylene composition which after a step of injection-moulding foaming featured by homogeneous surface appearance and balanced mechanical properties.

Therefore, it is an object of the present invention to provide a foamable polypropylene composition applicable for the preparation of a foamed article having homogeneous/good surface appearance and mechanical properties.

The finding of the present invention is to provide a polypropylene composition (C) comprising a heterophasic propylene copolymer and an inorganic filler.

Accordingly, the present invention is directed to a polypropylene composition (C), comprising

-   a) a first heterophasic propylene copolymer (HECO1) having a     comonomer content of the xylene soluble fraction (XCS) equal or     above 40.0 mol-%, said first heterophasic propylene copolymer     comprising     -   i) a first matrix being a first propylene polymer (M1) and     -   ii) a first elastomeric propylene copolymer (E1) being dispersed         in said first matrix, -   b) a second heterophasic propylene copolymer (HECO2) having a     comonomer content of the xylene soluble fraction (XCS) below 39.0     mol-%, said second heterophasic propylene copolymer comprising     -   iii) a second matrix being a second propylene polymer (M2) and     -   iv) a second elastomeric propylene copolymer (E1) being         dispersed in said second matrix, -   c) an inorganic filler (F), -   d) optionally a high density polyethylene (HDPE), and -   e) optionally a plastomer (PL) being a copolymer of ethylene and a     C₄ to C₈ α-olefin.

It was surprisingly found that a foamed part obtained from a polypropylene composition (C) comprising two different heterophasic propylene copolymers is featured by excellent mechanical properties and surface appearance. The dispersed phase of the heterophasic system can have a bimodal molecular weight distribution in order to assure good balance between mechanics and surface appearance. Additionally, a high density polyethylene (HDPE) and other additives can be used for improvement of the scratch resistance which is especially useful for interior applications. The compositions are suitable for chemical as well as physical foaming.

According to one embodiment of the present invention, the xylene soluble fraction (XCS) of the second heterophasic copolymer (HECO2) has an intrinsic viscosity (IV) above 3.5 dl/g.

According to another embodiment of the present invention, the polypropylene composition (C) comprises

-   a) 40.0 to 60.0 wt.-% of the first heterophasic propylene copolymer     (HECO1), -   b) 21.0 to 31.0 wt.-% of the second heterophasic propylene copolymer     (HECO2), -   c) 10.0 to 20.0 wt.-% of the inorganic filler (F), -   d) optionally 2.0 to 10.0 wt.-% of the high density polyethylene     (HDPE), and -   e) optionally 5.0 to 15.0 wt.-% of the plastomer (PL) being a     copolymer of ethylene and a C₄ to C₈ α-olefin, based on the overall     polypropylene composition (C).

According to a further embodiment of the present invention, the matrix of the first heterophasic propylene copolymer (HECO1) being the first propylene polymer (M1) has a melt flow rate MFR₂ (230° C.) determined according to ISO 1133 in the range of 120 to 500 g/10 min and the matrix of the second heterophasic propylene copolymer (HECO2) being the second propylene polymer (M2) has a melt flow rate MFR₂ (230° C.) determined according to ISO 1133 in the range of 40 to 170 g/10 min.

According to still another embodiment of the present invention, the first heterophasic propylene copolymer (HECO1) has

-   i) a melt flow rate MFR₂ (230° C.) determined according to ISO 1133     in the range of 50 to 90 g/10 min, and/or -   ii) a comonomer content in the range of 20.0 to 50.0 mol-%, and/or -   iii) a xylene soluble fraction (XCS) in the range of 10.0 to 35.0     wt.-%.

According to one embodiment of the present invention, the second heterophasic propylene copolymer (HECO2) has

-   i) a melt flow rate MFR₂ (230° C.) determined according to ISO 1133     in the range of 1.0 to 15 g/10 min, and/or -   ii) a comonomer content in the range of 5.0 to 30.0 mol-%, and/or -   iii) a xylene soluble fraction (XCS) in the range of 20.0 to 40.0     wt.-%.

It is especially preferred that the first propylene polymer (M1) and/or the second propylene polymer (M2) are propylene homopolymers.

According to one embodiment of the present invention, the first elastomeric propylene copolymer (E1) and/or the second elastomeric propylene copolymer (E2) are copolymers of propylene and ethylene.

According to another embodiment of the present invention, the polypropylene composition (C) has a melt flow rate MFR₂ (230° C.) determined according to ISO 1133 in the range of 10 to 40 g/10 min.

According to a further embodiment of the present invention, the plastomer (PL) is a copolymer of ethylene and 1-octene.

It is especially preferred that the inorganic filler (F) is talc and/or wollastonite.

According to one embodiment of the present invention, the polypropylene composition (C) is a foamable polypropylene composition.

The present invention is further directed to the use of the polypropylene composition (C) as described above for the production of a foamed article.

Further, the present invention is directed to a foamed article, comprising the polypropylene composition (C) as described above.

It is especially preferred that said foamed article is an automotive article.

In the following, the present invention is described in more detail.

The Polypropylene Composition (C)

The inventive polypropylene composition (C) comprises a first heterophasic propylene copolymer (HECO1) comprising a first matrix being a propylene polymer (M1) and a first elastomeric propylene copolymer (E1) and a second heterophasic propylene copolymer (HECO2) comprising a second matrix being a propylene polymer (M2) and a second elastomeric propylene copolymer (E2).

Accordingly, the inventive polypropylene composition (C) comprises a heterophasic system comprising matrix (M) formed by the first propylene polymer (M1) and the second propylene polymer (M2), and the first elastomeric propylene copolymer (E1) and the second elastomeric propylene copolymer (E2) are dispersed in said matrix (M). Thus the matrix (M) contains (finely) dispersed inclusions being not part of the matrix (M) and said inclusions contain the first elastomeric propylene copolymer (E1) and the second elastomeric propylene copolymer (E2). The term inclusion indicates that the matrix (M) and the inclusion form different phases as defined below.

Further, the inventive polypropylene composition comprises an inorganic filler (F).

Accordingly, it is preferred that the polypropylene composition (C) comprises, more preferably consists of, 60 to 95 wt.-% of the matrix (M), more preferably 70 to 90 wt.-%, still more preferably 75 to 80 wt.-% and 5 to 40 wt.-% of the dispersed phase comprising the first elastomeric propylene copolymer (E1) and the second elastomeric propylene copolymer (E2), more preferably 10 to 30 wt.-%, still more preferably 20 to 25 wt.-% and 10 to 20 wt.-% of the inorganic filler (F), more preferably 12 to 18 wt.-%, still more preferably 13 to 16 wt.-%, based on the overall weight of the polypropylene composition (C).

Preferably, the polypropylene composition (C) contains the first propylene polymer (M1) and the second propylene polymer (M2) forming the matrix (M) in a ratio of 1:1 to 3:1 and the first elastomeric propylene copolymer (E1) and the second elastomeric propylene copolymer (E2) in a ratio of 1:1 to 3:1. Accordingly, it is preferred that the polypropylene composition (C) comprises, 40 to 63 wt.-%, more preferably 46 to 60 wt.-%, still more preferably 50 to 53 wt.-% of the first propylene polymer (M1), 20 to 32 wt.-%, more preferably 23 to 30 wt.-%, still more preferably 25 to 27 wt.-% of the second propylene polymer (M2) and 3 to 26 wt.-%, more preferably 7 to 20 wt.-%, still more preferably 13 to 17 wt.-% of the first elastomeric propylene copolymer (E1) and 2 to 14 wt.-%, more preferably 3 to 10 wt.-%, still more preferably 6 to 8 wt.-% of the second elastomeric propylene copolymer (E2) and 10 to 20 wt.-% more preferably 12 to 18 wt.-%, still more preferably 13 to 16 wt.-% of the inorganic filler (F), based on the overall weight of the polypropylene composition (C).

According to a preferred embodiment of the present invention, the polypropylene composition (C) further comprises a high density polyethylene (HDPE) and a plastomer (PL) being a copolymer of ethylene and a C₄ to C₈ α-olefin. Accordingly, it is preferred that the polypropylene composition (C) comprises, 30 to 53 wt.-%, more preferably 36 to 50 wt.-%, still more preferably 40 to 43 wt.-% of the first propylene polymer (M1), 20 to 32 wt.-%, more preferably 23 to 30 wt.-%, still more preferably 25 to 27 wt.-% of the second propylene polymer (M2) and 3 to 20 wt.-%, more preferably 7 to 19 wt.-%, still more preferably 10 to 17 wt.-% of the first elastomeric propylene copolymer (E1) and 2 to 14 wt.-%, more preferably 3 to 10 wt.-%, still more preferably 6 to 8 wt.-% of the second elastomeric propylene copolymer (E2), 10 to 20 wt.-% more preferably 12 to 18 wt.-%, still more preferably 13 to 16 wt.-% of the inorganic filler (F), 2 to 10 wt.-%, more preferably 3 to 8 wt.-%, still more preferably 4 to 6 wt.-% of the high density polyethylene (HDPE) and 5 to 15 wt.-%, more preferably 6 to 11 wt.-%, still more preferably 7 to 9 wt.-% of the plastomer (PL), based on the overall weight of the polypropylene composition (C).

Preferably, the polypropylene composition (C) is obtained by a sequential polymerization process wherein at least two, like three, reactors are connected in series. For example, said process comprises the steps of

-   a) polymerizing propylene and optionally ethylene in a first reactor     (R1) to obtain the first propylene polymer (M1), -   b) transferring the first propylene polymer (M1) into a second     reactor (R2), -   c) polymerizing in said second reactor (R2) in the presence of said     first propylene polymer (M1) propylene and optionally ethylene     obtaining the second propylene polymer (M2), said first propylene     polymer (M1) and said second propylene polymer (M2) form the matrix     (M), -   d) transferring the matrix (M) into a third reactor (R3), -   e) polymerizing in said third reactor (R3) in the presence of the     matrix (M) propylene and/or a C₄ to C₈ α-olefin, obtaining a third     polymer fraction, said polymer fraction is the first elastomeric     copolymer (E1), -   f) transferring the matrix (M) and the first elastomeric copolymer     (E1) into a fourth reactor (R4), -   g) polymerizing in said fourth reactor (R4) in the presence of the     matrix (M) and the first elastomeric propylene copolymer (E1)     propylene and/or a C₄ to C₈ α-olefin, obtaining a fourth polymer     fraction, said polymer fraction is the second elastomeric copolymer     (E2), said matrix (M) and said first elastomeric propylene copolymer     (E1) and said second elastomeric propylene copolymer form a     heterophasic propylene copolymer, -   h) optionally melt blending said heterophasic propylene copolymer     obtained in the fourth reactor (R4) with the inorganic filler (F),     optionally the high density polyethylene (HDPE) and optionally the     plastomer (PL).

Alternatively, the polypropylene composition (C) is obtained by melt blending the first heterophasic propylene copolymer (HECO1) comprising a matrix being the first propylene polymer (M1) and a dispersed phase being the first elastomeric propylene copolymer (E1), the second heterophasic propylene copolymer (HECO2) comprising a matrix being the second propylene polymer (M2) and a dispersed phase being the second elastomeric propylene copolymer (E2), the inorganic filler (F), optionally the high density polyethylene (HDPE) and optionally the plastomer (PL). Melt blending of said first heterophasic propylene copolymer (HECO1) and said second heterophasic propylene copolymer (HECO2) results in a heterophasic system wherein the first propylene polymer (M1) and the second propylene polymer (M2) form the matrix and the first elastomeric propylene copolymer (E1) and the second elastomeric propylene copolymer (E2) form the dispersed phase.

It is especially preferred that the polypropylene composition (C) is obtained by melt blending said first heterophasic propylene copolymer (HECO1) and said second heterophasic propylene copolymer (HECO2) with the inorganic filler (F) and optionally the high density polyethylene (HDPE) and/or the plastomer (PL).

Accordingly, it is preferred that the polypropylene composition (C) comprises, 40 to 60 wt.-%, more preferably 41 to 59 wt.-%, still more preferably 42 to 57 wt.-% of the first heterophasic propylene copolymer (HECO1), 21 to 31 wt.-%, more preferably 23 to 30 wt.-%, still more preferably 25 to 27 wt.-% of the second heterophasic propylene copolymer (HECO2), 10 to 20 wt.-% more preferably 12 to 18 wt.-%, still more preferably 13 to 16 wt.-% of the inorganic filler (F), optionally 2 to 10 wt.-%, more preferably 3 to 8 wt.-%, still more preferably 4 to 6 wt.-% of the high density polyethylene (HDPE) and optionally 5 to 15 wt.-%, more preferably 6 to 11 wt.-%, still more preferably 7 to 9 wt.-% of the plastomer (PL), based on the overall weight of the polypropylene composition (C).

The polypropylene composition (C) of the present invention may include additives (AD). Accordingly, it is preferred that that the polypropylene composition (C) comprises, preferably consists of, 40 to 60 wt.-%, more preferably 41 to 59 wt.-%, still more preferably 42 to 57 wt.-% of the first heterophasic propylene copolymer (HECO1), 21 to 31 wt.-%, more preferably 23 to 30 wt.-%, still more preferably 25 to 27 wt.-% of the second heterophasic propylene copolymer (HECO2), 10 to 20 wt.-% more preferably 12 to 18 wt.-%, still more preferably 13 to 16 wt.-% of the inorganic filler (F), optionally 2 to 10 wt.-%, more preferably 3 to 8 wt.-%, still more preferably 4 to 6 wt.-% of the high density polyethylene (HDPE) and optionally 5 to 15 wt.-%, more preferably 6 to 11 wt.-%, still more preferably 7 to 9 wt.-% of the plastomer (PL) and 0.05 to 5 wt.-%, preferably 0.1 to 3 wt.-% of additives (AD), based on the overall weight of the polypropylene composition (C). The additives (AD) are described in more detail below.

Preferably the polypropylene composition (C) of the invention does not comprise (a) further polymer(s) different to the first propylene polymer (M1), the second propylene polymer (M2), the first elastomeric propylene copolymer (E1), the second elastomeric propylene copolymer (E2), the high density polyethylene (HDPE) and the plastomer (PL) in an amount exceeding 5.0 wt.-%, preferably in an amount exceeding 3.0 wt.-%, more preferably in an amount exceeding 2.5 wt.-%, based on the overall weight of the polypropylene composition (C).

It is preferred that the polypropylene composition (C) has a moderate melt flow rate. Thus, it is preferred that the melt flow rate MFR₂ (230° C.) determined according to ISO 1133 of the polypropylene composition (C) is in the range of 10 to 40 g/10 min, more preferably in the range of 15 to 35 g/10 min, still more preferably in the range of 20 to 32 g/10 min.

Further, it is preferred that the polypropylene composition (C) is featured by a rather high flexural modulus. Accordingly, it is preferred that the polypropylene composition (C) has a flexural modulus measured on injection moulded specimens according to ISO 178 in the range of 1000 to 3000 MPa, more preferably in the range of 1200 to 2800 MPa, still more preferably in the range of 1500 to 2700 MPa.

In the following, the first heterophasic propylene copolymer (HECO1), the second heterophasic propylene copolymer (HECO2), the high density polyethylene (HDPE), the plastomer (PL) and the inorganic filler (F) are described in more detail.

The First Heterophasic Propylene Copolymer (HECO1)

The inventive polypropylene composition (C) comprises a first heterophasic propylene copolymer (HECO1).

The first heterophasic propylene copolymer (HECO1) according to this invention comprises a matrix (M) being the first propylene polymer (M1) and dispersed therein an elastomeric propylene copolymer (E) being the first elastomeric propylene copolymer (E1). Thus the matrix (M) contains (finely) dispersed inclusions being not part of the matrix (M) and said inclusions contain the elastomeric propylene copolymer (E). The term inclusion indicates that the matrix (M) and the inclusion form different phases within the heterophasic propylene copolymer (HECO1). The presence of second phases or the so called inclusions are for instance visible by high resolution microscopy, like electron microscopy or atomic force microscopy, or by dynamic mechanical thermal analysis (DMTA). Specifically, in DMTA the presence of a multiphase structure can be identified by the presence of at least two distinct glass transition temperatures.

Accordingly, the first heterophasic composition (HECO1) according to this invention preferably comprises

-   (a) the (semi)crystalline first propylene polymer (M1) as the     matrix (M) and -   (b) the first elastomeric propylene copolymer (E1).

Preferably the weight ratio between the first propylene polymer (M1) and the elastomeric propylene copolymer (E1) [M1/E1] of the first heterophasic composition (HECO1) is in the range of 90/10 to 40/60, more preferably in the range of 85/15 to 45/55, yet more preferably in the range of 83/17 to 50/50, like in the range of 82/18 to 60/40.

Preferably, the first heterophasic propylene copolymer (HECO1) according to this invention comprises as polymer components only the first propylene polymer (M1) and the first elastomeric propylene copolymer (E1). In other words, the first heterophasic propylene copolymer (HECO1) may contain further additives but no other polymer in an amount exceeding 5.0 wt.-%, more preferably exceeding 3.0 wt.-%, like exceeding 1.0 wt.-%, based on the total first heterophasic propylene copolymer (HECO1). One additional polymer which may be present in such low amounts is a polyethylene which is a reaction by-product obtained by the preparation of the first heterophasic propylene copolymer (HECO1). Accordingly, it is in particular appreciated that the instant first heterophasic propylene copolymer (HECO1) contains only the first propylene polymer (M1), the first elastomeric propylene copolymer (E1) and optionally polyethylene in amounts as mentioned in this paragraph.

The first heterophasic propylene copolymer (HECO1) applied according to this invention is featured by a rather high melt flow rate. Accordingly, the first heterophasic propylene copolymer (HECO1) has a melt flow rate MFR₂ (230° C.) in the range of 50 to 90 g/10 min, preferably in the range of 60 to 80 g/10 min, more preferably in the range of 65 to 71 g/10 min.

Preferably, it is desired that the first heterophasic propylene copolymer (HECO1) is thermo mechanically stable. Accordingly, it is appreciated that the first heterophasic propylene copolymer (HECO1) has a melting temperature of at least 160° C., more preferably in the range of 160 to 167° C., still more preferably in the range of 162 to 165° C.

The first heterophasic propylene copolymer (HECO1) comprises apart from propylene also comonomers. Preferably the first heterophasic propylene copolymer (HECO1) comprises apart from propylene ethylene and/or C₄ to C₈ α-olefins. Accordingly, the term “propylene copolymer” according to this invention is understood as a polypropylene comprising, preferably consisting of, units derivable from

(a) propylene

and

(b) ethylene and/or C₄ to C₈ α-olefins.

Thus, the first heterophasic propylene copolymer (HECO1), i.e. first propylene polymer (M1) as well as the first elastomeric propylene copolymer (E1), can comprise monomers copolymerizable with propylene, for example comonomers such as ethylene and/or C₄ to C₈ α-olefins, in particular ethylene and/or C₄ to C₈ α-olefins, e.g. 1-butene and/or 1-hexene. Preferably, the first heterophasic propylene copolymer (HECO1) according to this invention comprises, especially consists of, monomers copolymerizable with propylene from the group consisting of ethylene, 1-butene and 1-hexene. More specifically, the first heterophasic propylene copolymer (HECO1) of this invention comprises—apart from propylene—units derivable from ethylene and/or 1-butene. In a preferred embodiment, the first heterophasic propylene copolymer (HECO1) according to this invention comprises units derivable from ethylene and propylene only. Still more preferably the first propylene polymer (M1) as well as the first elastomeric propylene copolymer (E1) of the first heterophasic propylene copolymer (HECO1) contain the same comonomers, like ethylene.

Additionally, it is appreciated that the first heterophasic propylene copolymer (HECO1) preferably has a rather low total comonomer content, preferably ethylene content. Thus, it is preferred that the comonomer content of the first heterophasic propylene copolymer (HECO1) is in the range from 4.0 to 25.0 mol-%, preferably in the range from 6.0 to 18.0 mol-%, more preferably in the range from 10.0 to 13.0 mol-%.

The xylene cold soluble (XCS) fraction measured according to according ISO 16152 (25° C.) of the first heterophasic propylene copolymer (HECO1) is in the range of 10.0 to 40.0 wt.-%, preferably in the range from 15.0 to 30.0 wt.-%, more preferably in the range from 17.0 to 25.0 wt.-%, still more preferably in the range from 19.0 to 22.0 wt.-%.

Further it is appreciated that the xylene cold soluble (XCS) fraction of the first heterophasic propylene copolymer (HECO1) is specified by its intrinsic viscosity. A low intrinsic viscosity (IV) value reflects a low weight average molecular weight. For the present invention it is appreciated that the xylene cold soluble fraction (XCS) of the first heterophasic propylene copolymer (HECO1) has an intrinsic viscosity (IV) measured according to ISO 1628/1 (at 135° C. in decalin) in the range of 1.0 to 3.3 dl/g, preferably in the range of 1.5 to 3.2 dl/g, more preferably in the range of 1.7 to 3.0 dl/g.

Additionally, it is preferred that the comonomer content, i.e. ethylene content, of the xylene cold soluble (XCS) fraction of the first heterophasic propylene copolymer (HECO1) is equal or above 40 mol-%, preferably in the range of 40 to 55 mol-%, more preferably in the range of 42 to 50 mol.-%, yet more preferably in the range of 43 to 46 mol.-%. The comonomers present in the xylene cold soluble (XCS) fraction are those defined above for the first propylene polymer (M1) and the first elastomeric propylene copolymer (E1), respectively. In one preferred embodiment the comonomer is ethylene only.

The first heterophasic propylene copolymer (HECO1) can be further defined by its individual components, i.e. the first propylene polymer (M1) and the first elastomeric propylene copolymer (E1).

The first propylene polymer (M1) can be a propylene copolymer or a propylene homopolymer, the latter being preferred.

In case the first propylene polymer (M1) is a propylene copolymer, the first propylene polymer (M1) comprises monomers copolymerizable with propylene, for example comonomers such as ethylene and/or C₄ to C₈ α-olefins, in particular ethylene and/or C₄ to C₆ α-olefins, e.g. 1-butene and/or 1-hexene. Preferably the first propylene polymer (M1) according to this invention comprises, especially consists of, monomers copolymerizable with propylene from the group consisting of ethylene, 1-butene and 1-hexene. More specifically the first propylene polymer (M1) of this invention comprises—apart from propylene—units derivable from ethylene and/or 1-butene. In a preferred embodiment the first propylene polymer (M1) comprises units derivable from ethylene and propylene only.

The first propylene polymer (M1) according to this invention has a melt flow rate MFR₂ (230° C./2.16 kg) measured according to ISO 1133 in the range of 120 to 500 g/10 min, more preferably in the range of 130 to 200 g/10 min, still more preferably in the range of 140 to 170 g/10 min.

As mentioned above the first heterophasic propylene copolymer (HECO1) is featured by a low comonomer content. Accordingly, the comonomer content of the first propylene polymer (M1) is in the range of 0.0 to 5.0 mol-%, yet more preferably in the range of 0.0 to 3.0 mol-%, still more preferably in the range of 0.0 to 1.0 mol-%. It is especially preferred that the first propylene polymer (M1) is a propylene homopolymer.

The first heterophasic propylene copolymer (HECO1) preferably comprises 60 to 95 wt.-%, more preferably 60 to 90 wt.-%, still more preferably 65 to 87 wt.-% of the first propylene polymer (M1), based on the total weight of the first heterophasic propylene copolymer (HECO1).

Additionally, the first heterophasic propylene copolymer (HECO1) preferably comprises 5 to 40 wt.-%, more preferably 10 to 40 wt.-%, still more preferably 13 to 35 wt.-% of the first elastomeric propylene copolymer (E1), based on the total weight of the first heterophasic propylene copolymer (HECO1).

Thus, it is appreciated that the first heterophasic propylene copolymer (HECO1) preferably comprises, more preferably consists of, 60 to 95 wt.-%, preferably 60 to 90 wt.-%, more preferably 65.0 to 87.0 wt.-% of the first propylene polymer (M1) and 5 to 40 wt.-%, preferably 10 to 40 wt.-%, more preferably 13.0 to 35.0 wt.-% of the first elastomeric propylene copolymer (E1), based on the total weight of the first heterophasic propylene copolymer (HECO1).

Accordingly, a further component of the first heterophasic propylene copolymer (HECO1) is the elastomeric propylene copolymer (E1) dispersed in the matrix (M) being the first propylene polymer (M1). Concerning the comonomers used in the first elastomeric propylene copolymer (E1) it is referred to the information provided for the first heterophasic propylene copolymer (HECO1). Accordingly, the first elastomeric propylene copolymer (E1) comprises monomers copolymerizable with propylene, for example comonomers such as ethylene and/or C₄ to C₈ α-olefins, in particular ethylene and/or C₄ to C₆ α-olefins, e.g. 1-butene and/or 1-hexene. Preferably, the first elastomeric propylene copolymer (E1) comprises, especially consists of, monomers copolymerizable with propylene from the group consisting of ethylene, 1-butene and 1-hexene. More specifically, the first elastomeric propylene copolymer (E1) comprises—apart from propylene—units derivable from ethylene and/or 1-butene. Thus, in an especially preferred embodiment the first elastomeric propylene copolymer (E1) comprises units derivable from ethylene and propylene only.

The comonomer content of the first elastomeric propylene copolymer (E1) preferably is in the range of 35.0 to 70.0 mol-%, more preferably in the range of 37.0 to 60.0 mol-%, still more preferably in the range of 40.0 to 50.0 mol-%.

The first heterophasic propylene copolymer (HECO1) as defined in the instant invention may contain up to 5.0 wt.-% additives, like nucleating agents and antioxidants, as well as slip agents and antiblocking agents. Preferably the additive content (without α-nucleating agents) is below 3.0 wt.-%, like below 1.0 wt.-%.

According to a preferred embodiment of the present invention, the first heterophasic propylene copolymer (HECO1) contains an α-nucleating agent.

According to this invention the alpha nucleating agent is not an additive (AD).

The alpha-nucleating agent is preferably selected from the group consisting of

-   (i) salts of monocarboxylic acids and polycarboxylic acids, e.g.     sodium benzoate or aluminum tert-butylbenzoate, and -   (ii) dibenzylidenesorbitol (e.g. 1,3:2,4 dibenzylidenesorbitol) and     C₁-C₈-alkyl-substituted dibenzylidenesorbitol derivatives, such as     methyldibenzylidenesorbitol, ethyldibenzylidenesorbitol or     dimethyldibenzylidenesorbitol (e.g. 1,3:2,4 di(methylbenzylidene)     sorbitol), or substituted nonitol-derivatives, such as     1,2,3,-trideoxy-4,6:5,7-bis-O-[(4-propylphenyl)methylene]-nonitol,     and -   (iii) salts of diesters of phosphoric acid, e.g. sodium     2,2′-methylenebis (4,6-di-tert-butylphenyl) phosphate or     aluminium-hydroxy-bis[2,2′-methylene-bis(4,6-di-t-butylphenyl)phosphate],     and -   (iv) vinylcycloalkane polymer or vinylalkane polymer, and -   (v) mixtures thereof.

Preferably the alpha-nucleating agent comprised in the composition of the invention is vinylcycloalkane polymer and/or vinylalkane polymer, more preferably vinylcycloalkane polymer, like vinylcyclohexane (VCH) polymer. Vinyl cyclohexane (VCH) polymer is particularly preferred as α-nucleating agent. It is appreciated that the amount of vinylcycloalkane, like vinylcyclohexane (VCH), polymer and/or vinylalkane polymer, more preferably of vinylcyclohexane (VCH) polymer, in the composition is not more than 500 ppm, preferably not more than 200 ppm, more preferably not more than 100 ppm, like in the range of 0.1 to 500 ppm, preferably in the range of 0.5 to 200 ppm, more preferably in the range of 1 to 100 ppm. Furthermore, it is appreciated that the vinylcycloalkane polymer and/or vinylalkane polymer is introduced into the composition by the BNT technology. With regard to the BNT-technology reference is made to the international applications WO 99/24478, WO 99/24479 and particularly WO 00/68315. According to this technology a catalyst system, preferably a Ziegler-Natta procatalyst, can be modified by polymerizing a vinyl compound in the presence of the catalyst system, comprising in particular the special Ziegler-Natta procatalyst, an external donor and a cocatalyst, which vinyl compound has the formula: CH₂═CH—CHR³R⁴ wherein R³ and R⁴ together form a 5- or 6-membered saturated, unsaturated or aromatic ring or independently represent an alkyl group comprising 1 to 4 carbon atoms, and the modified catalyst is preferably used for the preparation of the heterophasic composition (HECO) present in the modified polypropylene composition (mPP). The polymerized vinyl compound acts as an alpha-nucleating agent. The weight ratio of vinyl compound to solid catalyst component in the modification step of the catalyst is preferably of up to 5 (5:1), more preferably up to 3 (3:1), like in the range of 0.5 (1:2) to 2 (2:1).

Such nucleating agents are commercially available and are described, for example, in “Plastic Additives Handbook”, 5th edition, 2001 of Hans Zweifel (pages 967 to 990).

The first heterophasic propylene copolymer (HECO1) can be produced by blending the first propylene polymer (M1) and the first elastomeric propylene copolymer (E1). However, it is preferred that the first heterophasic propylene copolymer (HECO1) is produced in a sequential step process, using reactors in serial configuration and operating at different reaction conditions. As a consequence, each fraction prepared in a specific reactor may have its own molecular weight distribution and/or comonomer content distribution.

The first heterophasic propylene copolymer (HECO1) according to this invention is preferably produced in a sequential polymerization process, i.e. in a multistage process, known in the art, wherein the first propylene polymer (M1) is produced at least in one slurry reactor, preferably in a slurry reactor and optionally in a subsequent gas phase reactor, and subsequently the first elastomeric propylene copolymer (E1) is produced at least in one, i.e. one or two, gas phase reactor(s).

Accordingly it is preferred that the first heterophasic propylene copolymer (HECO1) is produced in a sequential polymerization process comprising the steps of

-   (a) polymerizing propylene and optionally at least one ethylene     and/or C₄ to C₁₂ α-olefin in a first reactor (R1) obtaining the     first polypropylene fraction of the first propylene polymer (M1),     preferably said first polypropylene fraction is a propylene     homopolymer, -   (b) transferring the first polypropylene fraction into a second     reactor (R2), -   (c) polymerizing in the second reactor (R2) and in the presence of     said first polypropylene fraction propylene and optionally at least     one ethylene and/or C₄ to C₁₂ α-olefin obtaining thereby the second     polypropylene fraction, preferably said second polypropylene     fraction is a second propylene homopolymer, said first polypropylene     fraction and said second polypropylene fraction form the first     propylene polymer (M1), i.e. the matrix of the first heterophasic     propylene copolymer (HECO1), -   (d) transferring the first propylene polymer (M1) of step (c) into a     third reactor (R3), -   (e) polymerizing in the third reactor (R3) and in the presence of     the first propylene polymer (M1) obtained in step (c) propylene and     ethylene to obtain the first elastomeric propylene copolymer (E1)     dispersed in the first propylene polymer (M1), the first propylene     polymer (M1) and the first elastomeric propylene copolymer (E1) form     the first heterophasic propylene copolymer (HECO1).

Of course, in the first reactor (R1) the second polypropylene fraction can be produced and in the second reactor (R2) the first polypropylene fraction can be obtained. The same holds true for the elastomeric propylene copolymer phase.

Preferably between the second reactor (R2) and the third reactor (R3) the monomers are flashed out.

The term “sequential polymerization process” indicates that the first heterophasic propylene copolymer (HECO1) is produced in at least two, like three or four reactors connected in series. Accordingly, the present process comprises at least a first reactor (R1) and a second reactor (R2), more preferably a first reactor (R1), a second reactor (R2), and a third reactor (R3). The term “polymerization reactor” shall indicate that the main polymerization takes place. Thus in case the process consists of four polymerization reactors, this definition does not exclude the option that the overall process comprises for instance a pre-polymerization step in a pre-polymerization reactor. The term “consist of” is only a closing formulation in view of the main polymerization reactors.

The first reactor (R1) is preferably a slurry reactor (SR) and can be any continuous or simple stirred batch tank reactor or loop reactor operating in bulk or slurry. Bulk means a polymerization in a reaction medium that comprises of at least 60% (w/w) monomer. According to the present invention the slurry reactor (SR) is preferably a (bulk) loop reactor (LR).

The second reactor (R2) can be a slurry reactor, like a loop reactor, as the first reactor or alternatively a gas phase reactor (GPR).

The third reactor (R3) is preferably a gas phase reactor (GPR).

Such gas phase reactors (GPR) can be any mechanically mixed or fluid bed reactors. Preferably the gas phase reactors (GPR) comprise a mechanically agitated fluid bed reactor with gas velocities of at least 0.2 m/sec. Thus it is appreciated that the gas phase reactor is a fluidized bed type reactor preferably with a mechanical stirrer.

Thus in a preferred embodiment the first reactor (R1) is a slurry reactor (SR), like a loop reactor (LR), whereas the second reactor (R2) and the third reactor (R3) are gas phase reactors (GPR). Accordingly for the instant process at least three, preferably three polymerization reactors, namely a slurry reactor (SR), like a loop reactor (LR), a first gas phase reactor (GPR-1) and a second gas phase reactor (GPR-2) connected in series are used. If needed prior to the slurry reactor (SR) a pre-polymerization reactor is placed.

In another preferred embodiment the first reactor (R1) and second reactor (R2) are slurry reactors (SR), like a loop reactors (LR), whereas the third reactor (R3) is a gas phase reactors (GPR). Accordingly for the instant process at least three, preferably three polymerization reactors, namely two slurry reactors (SR), like two loop reactors (LR), and a gas phase reactor (GPR-1) connected in series are used. If needed prior to the first slurry reactor (SR) a pre-polymerization reactor is placed.

A preferred multistage process is a “loop-gas phase”-process, such as developed by Borealis A/S, Denmark (known as BORSTAR® technology) described e.g. in patent literature, such as in EP 0 887 379, WO 92/12182 WO 2004/000899, WO 2004/111095, WO 99/24478, WO 99/24479 or in WO 00/68315.

A further suitable slurry-gas phase process is the Spheripol® process of Basell.

Preferably, in the instant process for producing the first heterophasic propylene copolymer (HECO1) as defined above the conditions for the first reactor (R1), i.e. the slurry reactor (SR), like a loop reactor (LR), of step (a) may be as follows:

-   -   the temperature is within the range of 50° C. to 110° C.,         preferably between 60° C. and 100° C., more preferably between         68 and 95° C.,     -   the pressure is within the range of 20 bar to 80 bar, preferably         between 40 bar to 70 bar,     -   hydrogen can be added for controlling the molar mass in a manner         known per se.

Subsequently, the reaction mixture from step (a) is transferred to the second reactor (R2), i.e. gas phase reactor (GPR-1), i.e. to step (c), whereby the conditions in step (c) are preferably as follows:

-   -   the temperature is within the range of 50° C. to 130° C.,         preferably between 60° C. and 100° C.,     -   the pressure is within the range of 5 bar to 50 bar, preferably         between 15 bar to 35 bar,     -   hydrogen can be added for controlling the molar mass in a manner         known per se.

The condition in the third reactor (R3), preferably in the second gas phase reactor (GPR-2) is similar to the second reactor (R2).

The residence time can vary in the three reactor zones.

In one embodiment of the process for producing the polypropylene the residence time in bulk reactor, e.g. loop is in the range 0.1 to 2.5 hours, e.g. 0.15 to 1.5 hours and the residence time in gas phase reactor will generally be 0.2 to 6.0 hours, like 0.5 to 4.0 hours.

If desired, the polymerization may be effected in a known manner under supercritical conditions in the first reactor (R1), i.e. in the slurry reactor (SR), like in the loop reactor (LR), and/or as a condensed mode in the gas phase reactors (GPR).

Preferably the process comprises also a prepolymerization with the catalyst system, as described in detail below, comprising a Ziegler-Natta procatalyst, an external donor and optionally a cocatalyst.

In a preferred embodiment, the prepolymerization is conducted as bulk slurry polymerization in liquid propylene, i.e. the liquid phase mainly comprises propylene, with minor amount of other reactants and optionally inert components dissolved therein.

The prepolymerization reaction is typically conducted at a temperature of 10 to 60° C., preferably from 15 to 50° C., and more preferably from 20 to 45° C.

The pressure in the prepolymerization reactor is not critical but must be sufficiently high to maintain the reaction mixture in liquid phase. Thus, the pressure may be from 20 to 100 bar, for example 30 to 70 bar.

The catalyst components are preferably all introduced to the prepolymerization step. However, where the solid catalyst component (i) and the cocatalyst (ii) can be fed separately it is possible that only a part of the cocatalyst is introduced into the prepolymerization stage and the remaining part into subsequent polymerization stages. Also in such cases it is necessary to introduce so much cocatalyst into the prepolymerization stage that a sufficient polymerization reaction is obtained therein.

It is possible to add other components also to the prepolymerization stage. Thus, hydrogen may be added into the prepolymerization stage to control the molecular weight of the prepolymer as is known in the art. Further, antistatic additive may be used to prevent the particles from adhering to each other or to the walls of the reactor.

The precise control of the prepolymerization conditions and reaction parameters is within the skill of the art.

According to the invention the heterophasic composition (HECO1) is obtained by a multistage polymerization process, as described above, in the presence of a catalyst system comprising as component (i) a Ziegler-Natta procatalyst which contains a trans-esterification product of a lower alcohol and a phthalic ester.

The procatalyst used according to the invention for preparing the heterophasic composition (HECO1) is prepared by

a) reacting a spray crystallized or emulsion solidified adduct of MgCl₂ and a C₁-C₂ alcohol with TiCl₄

b) reacting the product of stage a) with a dialkylphthalate of formula (I)

-   -   wherein R^(1′) and R^(2′) are independently at least a C₅ alkyl         under conditions where a transesterification between said C₁ to         C₂ alcohol and said dialkylphthalate of formula (I) takes place         to form the internal donor         c) washing the product of stage b) or         d) optionally reacting the product of step c) with additional         TiCl₄

The procatalyst is produced as defined for example in the patent applications WO 87/07620, WO 92/19653, WO 92/19658 and EP 0 491 566. The content of these documents is herein included by reference.

First an adduct of MgCl₂ and a C₁-C₂ alcohol of the formula MgCl₂*nROH, wherein R is methyl or ethyl and n is 1 to 6, is formed. Ethanol is preferably used as alcohol.

The adduct, which is first melted and then spray crystallized or emulsion solidified, is used as catalyst carrier.

In the next step the spray crystallized or emulsion solidified adduct of the formula MgCl₂*nROH, wherein R is methyl or ethyl, preferably ethyl and n is 1 to 6, is contacting with TiCl₄ to form a titanized carrier, followed by the steps of

-   -   adding to said titanised carrier     -   (i) a dialkylphthalate of formula (I) with R^(1′) and R^(2′)         being independently at least a C₈-alkyl, like at least a         C₈-alkyl,     -   or preferably     -   (ii) a dialkylphthalate of formula (I) with R^(1′) and R^(2′)         being the same and being at least a C₈-alkyl, like at least a         C₈-alkyl,     -   or more preferably     -   (iii) a dialkylphthalate of formula (I) selected from the group         consisting of propylhexylphthalate (PrHP), dioctylphthalate         (DOP), di-iso-decylphthalate (DIDP), and ditridecylphthalate         (DTDP), yet more preferably the dialkylphthalate of formula (I)         is a dioctylphthalate (DOP), like di-iso-octylphthalate or         diethylhexylphthalate, in particular diethylhexylphthalate,     -   to form a first product,     -   subjecting said first product to suitable transesterification         conditions, i.e. to a temperature above 100° C., preferably         between 100 to 150° C., more preferably between 130 to 150° C.,         such that said methanol or ethanol is transesterified with said         ester groups of said dialkylphthalate of formula (I) to form         preferably at least 80 mol-%, more preferably 90 mol-%, most         preferably 95 mol.-%, of a dialkylphthalate of formula (II)

-   -   with R¹ and R² being methyl or ethyl, preferably ethyl, the         dialkylphthalat of formula (II) being the internal donor and     -   recovering said transesterification product as the procatalyst         composition (component (i)).

The adduct of the formula MgCl₂*nROH, wherein R is methyl or ethyl and n is 1 to 6, is in a preferred embodiment melted and then the melt is preferably injected by a gas into a cooled solvent or a cooled gas, whereby the adduct is crystallized into a morphologically advantageous form, as for example described in WO 87/07620.

This crystallized adduct is preferably used as the catalyst carrier and reacted to the procatalyst useful in the present invention as described in WO 92/19658 and WO 92/19653.

As the catalyst residue is removed by extracting, an adduct of the titanised carrier and the internal donor is obtained, in which the group deriving from the ester alcohol has changed.

In case sufficient titanium remains on the carrier, it will act as an active element of the procatalyst.

Otherwise the titanization is repeated after the above treatment in order to ensure a sufficient titanium concentration and thus activity.

Preferably the procatalyst used according to the invention contains 2.5 wt.-% of titanium at the most, preferably 2.2% wt.-% at the most and more preferably 2.0 wt.-% at the most. Its donor content is preferably between 4 to 12 wt.-% and more preferably between 6 and 10 wt.-%.

More preferably the procatalyst used according to the invention has been produced by using ethanol as the alcohol and dioctylphthalate (DOP) as dialkylphthalate of formula (I), yielding diethyl phthalate (DEP) as the internal donor compound.

Still more preferably the catalyst used according to the invention is the catalyst as described in the example section; especially with the use of dioctylphthalate as dialkylphthalate of formula (I).

For the production of the heterophasic composition (HECO1) according to the invention the catalyst system used preferably comprises in addition to the special Ziegler-Natta procatalyst an organometallic cocatalyst as component (ii).

Accordingly it is preferred to select the cocatalyst from the group consisting of trialkylaluminium, like triethylaluminium (TEA), dialkyl aluminium chloride and alkyl aluminium sesquichloride.

Component (iii) of the catalysts system used is an external donor represented by formula (IIIa) or (IIIb). Formula (IIIa) is defined by Si(OCH₃)₂R₂ ⁵  (IIIa) wherein R⁵ represents a branched-alkyl group having 3 to 12 carbon atoms, preferably a branched-alkyl group having 3 to 6 carbon atoms, or a cyclo-alkyl having 4 to 12 carbon atoms, preferably a cyclo-alkyl having 5 to 8 carbon atoms.

It is in particular preferred that R⁵ is selected from the group consisting of iso-propyl, iso-butyl, iso-pentyl, tert.-butyl, tert.-amyl, neopentyl, cyclopentyl, cyclohexyl, methylcyclopentyl and cycloheptyl.

Formula (IIIb) is defined by Si(OCH₂CH₃)₃(NR^(x)R^(y))  (IIIb) wherein R^(x) and R^(y) can be the same or different a represent a hydrocarbon group having 1 to 12 carbon atoms.

R^(x) and R^(y) are independently selected from the group consisting of linear aliphatic hydrocarbon group having 1 to 12 carbon atoms, branched aliphatic hydrocarbon group having 1 to 12 carbon atoms and cyclic aliphatic hydrocarbon group having 1 to 12 carbon atoms. It is in particular preferred that R^(x) and R^(y) are independently selected from the group consisting of methyl, ethyl, n-propyl, n-butyl, octyl, decanyl, iso-propyl, iso-butyl, iso-pentyl, tert.-butyl, tert.-amyl, neopentyl, cyclopentyl, cyclohexyl, methylcyclopentyl and cycloheptyl.

More preferably both R^(x) and R^(y) are the same, yet more preferably both R^(x) and R^(y) are an ethyl group.

More preferably the external donor is of formula (IIIa), like dicyclopentyl dimethoxy silane [Si(OCH₃)₂(cyclo-pentyl)₂], diisopropyl dimethoxy silane [Si(OCH₃)₂(CH(CH₃)₂)₂].

Most preferably the external donor is dicyclopentyl dimethoxy silane [Si(OCH₃)₂(cyclo-pentyl)₂].

In a further embodiment, the Ziegler-Natta procatalyst can be modified by polymerising a vinyl compound in the presence of the catalyst system, comprising the special Ziegler-Natta procatalyst (component (i)), an external donor (component (iii) and optionally a cocatalyst (component (iii)), which vinyl compound has the formula: CH₂═CH—CHR³R⁴ wherein R³ and R⁴ together form a 5- or 6-membered saturated, unsaturated or aromatic ring or independently represent an alkyl group comprising 1 to 4 carbon atoms, and the modified catalyst is used for the preparation of the heterophasic composition (HECO) according to this invention. The polymerized vinyl compound can act as an α-nucleating agent.

Concerning the modification of catalyst reference is made to the international applications WO 99/24478, WO 99/24479 and particularly WO 00/68315, incorporated herein by reference with respect to the reaction conditions concerning the modification of the catalyst as well as with respect to the polymerization reaction.

The Second Heterophasic Propylene Copolymer (HECO2)

The inventive polypropylene composition (C) further comprises a second heterophasic propylene copolymer (HECO2).

The second heterophasic propylene copolymer (HECO2) according to this invention comprises a matrix (M) being the second propylene polymer (M2) and dispersed therein an elastomeric propylene copolymer (E) being the second elastomeric propylene copolymer (E2). Thus the matrix (M) contains (finely) dispersed inclusions being not part of the matrix (M) and said inclusions contain the elastomeric propylene copolymer (E). Regarding the term inclusion, reference is made to the definition provided above.

Accordingly, the second heterophasic composition (HECO2) according to this invention preferably comprises

(a) the (semi)crystalline second propylene polymer (M2) as the matrix (M) and

(b) the second elastomeric propylene copolymer (E2).

Preferably the weight ratio between the second propylene polymer (M2) and the elastomeric propylene copolymer (E2) [M2/E2] of the second heterophasic propylene copolymer (HECO2) is in the range of 90/10 to 40/60, more preferably in the range of 85/15 to 45/55, yet more preferably in the range of 83/17 to 50/50, like in the range of 75/25 to 60/40.

Preferably, the second heterophasic propylene copolymer (HECO2) according to this invention comprises as polymer components only the second propylene polymer (M2) and the first elastomeric propylene copolymer (E2). In other words, the second heterophasic propylene copolymer (HECO2) may contain further additives but no other polymer in an amount exceeding 5.0 wt.-%, more preferably exceeding 3.0 wt.-%, like exceeding 1.0 wt.-%, based on the total second heterophasic propylene copolymer (HECO2). One additional polymer which may be present in such low amounts is a polyethylene which is a reaction by-product obtained by the preparation of the second heterophasic propylene copolymer (HECO2). Accordingly, it is in particular appreciated that the instant second heterophasic propylene copolymer (HECO2) contains only the second propylene polymer (M2), the second elastomeric propylene copolymer (E2) and optionally polyethylene in amounts as mentioned in this paragraph.

The second heterophasic propylene copolymer (HECO2) applied according to this invention is featured by a rather low melt flow rate. Accordingly, the second heterophasic propylene copolymer (HECO2) has a melt flow rate MFR₂ (230° C.) in the range of 1.0 to 20 g/10 min, preferably in the range of 3.0 to 15 g/10 min, more preferably in the range of 5.0 to 10 g/10 min.

Preferably, it is desired that the second heterophasic propylene copolymer (HECO2) is thermo mechanically stable. Accordingly, it is appreciated that the second heterophasic propylene copolymer (HECO2) has a melting temperature of at least 162° C., more preferably in the range of 163 to 167° C., still more preferably in the range of 163 to 165° C.

The second heterophasic propylene copolymer (HECO2) comprises apart from propylene also comonomers. Preferably the second heterophasic propylene copolymer (HECO2) comprises apart from propylene ethylene and/or C₄ to C₈ α-olefins. Regarding term “propylene copolymer”, reference is made to the definition provided above.

Thus, the second heterophasic propylene copolymer (HECO2), i.e. second propylene polymer (M2) as well as the second elastomeric propylene copolymer (E2), can comprise monomers copolymerizable with propylene, for example comonomers such as ethylene and/or C₄ to C₈ α-olefins, in particular ethylene and/or C₄ to C₈ α-olefins, e.g. 1-butene and/or 1-hexene. Preferably, the second heterophasic propylene copolymer (HECO2) according to this invention comprises, especially consists of, monomers copolymerizable with propylene from the group consisting of ethylene, 1-butene and 1-hexene. More specifically, the second heterophasic propylene copolymer (HECO2) of this invention comprises—apart from propylene—units derivable from ethylene and/or 1-butene. In a preferred embodiment, the second heterophasic propylene copolymer (HECO2) according to this invention comprises units derivable from ethylene and propylene only. Still more preferably the second propylene polymer (M1) as well as the second elastomeric propylene copolymer (E2) of the second heterophasic propylene copolymer (HECO2) contain the same comonomers, like ethylene.

Additionally, it is appreciated that the second heterophasic propylene copolymer (HECO2) preferably has a rather low total comonomer content, preferably ethylene content. Thus, it is preferred that the comonomer content of the second heterophasic propylene copolymer (HECO2) is in the range from 5.0 to 30.0 mol-%, preferably in the range from 6.0 to 18.0 mol-%, more preferably in the range from 7.0 to 13.0 mol-%.

The xylene cold soluble (XCS) fraction measured according to according ISO 16152 (25° C.) of the second heterophasic propylene copolymer (HECO2) is in the range of 15.0 to 40.0 wt.-%, preferably in the range from 17.0 to 35.0 wt.-%, more preferably in the range from 20.0 to 33.0 wt.-%, still more preferably in the range from 23.0 to 30.0 wt.-%.

Further it is appreciated that the xylene cold soluble (XCS) fraction of the second heterophasic propylene copolymer (HECO2) is specified by its intrinsic viscosity. A low intrinsic viscosity (IV) value reflects a low weight average molecular weight. For the present invention it is appreciated that the xylene cold soluble fraction (XCS) of the second heterophasic propylene copolymer (HECO2) has an intrinsic viscosity (IV) measured according to ISO 1628/1 (at 135° C. in decalin) above 3.5 dl/g. More preferably, the second heterophasic propylene copolymer (HECO2) has an intrinsic viscosity (IV) in the range of 3.5 to 9.0 dl/g, preferably in the range of 3.7 to 8.5 dl/g, more preferably in the range of 3.9.0 to 8.0 dl/g.

Additionally, it is preferred that the comonomer content, i.e. ethylene content, of the xylene cold soluble (XCS) fraction of the second heterophasic propylene copolymer (HECO2) is below 39 mol-%, preferably in the range of 20 to 38 mol-%, more preferably in the range of 23 to 35 mol.-%, yet more preferably in the range of 25 to 29 mol.-%. The comonomers present in the xylene cold soluble (XCS) fraction are those defined above for the second propylene polymer (M2) and the second elastomeric propylene copolymer (E2), respectively. In one preferred embodiment the comonomer is ethylene only.

The second heterophasic propylene copolymer (HECO2) can be further defined by its individual components, i.e. the second propylene polymer (M2) and the second elastomeric propylene copolymer (E2).

The second propylene polymer (M2) can be a propylene copolymer or a propylene homopolymer, the latter being preferred.

In case the second propylene polymer (M2) is a propylene copolymer, the second propylene polymer (M2) comprises monomers copolymerizable with propylene, for example comonomers such as ethylene and/or C₄ to C₈ α-olefins, in particular ethylene and/or C₄ to C₆ α-olefins, e.g. 1-butene and/or 1-hexene. Preferably the second propylene polymer (M2) according to this invention comprises, especially consists of, monomers copolymerizable with propylene from the group consisting of ethylene, 1-butene and 1-hexene. More specifically the second propylene polymer (M2) of this invention comprises—apart from propylene—units derivable from ethylene and/or 1-butene. In a preferred embodiment the second propylene polymer (M2) comprises units derivable from ethylene and propylene only.

The second propylene polymer (M2) according to this invention has a melt flow rate MFR₂ (230° C./2.16 kg) measured according to ISO 1133 in the range of 70 to 300 g/10 min, more preferably in the range of 75 to 250 g/10 min, still more preferably in the range of 80 to 200 g/10 min.

As mentioned above the second heterophasic propylene copolymer (HECO2) is featured by a low comonomer content. Accordingly, the comonomer content of the second propylene polymer (M2) is in the range of 0.0 to 5.0 mol-%, yet more preferably in the range of 0.0 to 3.0 mol-%, still more preferably in the range of 0.0 to 1.0 mol-%. It is especially preferred that the second propylene polymer (M2) is a propylene homopolymer.

The second propylene polymer (M2) preferably comprises at least two polymer fractions, like two or three polymer fractions, all of them are propylene homopolymers. Even more preferred the second propylene polymer (M2) comprises, preferably consists of, a first propylene homopolymer fraction (H-PP1) and a second propylene homopolymer fraction (H-PP2).

Preferably, the first propylene homopolymer fraction (H-PP1) and the second propylene homopolymer fraction (H-PP2) differ in melt flow rate.

Accordingly, one of the propylene homopolymer fractions (H-PP1) and (H-PP2) of the second propylene polymer (M2) is the low melt flow rate MFR₂ (230° C./2.16 kg) fraction and the other fraction is the high melt flow rate MFR₂ (230° C./2.16 kg) fraction, wherein further the low flow fraction and the high flow fraction fulfil in equation (I), more preferably in equation (Ia), still more preferably in equation (Ib),

$\begin{matrix} {{\frac{{MFR}({high})}{{MFR}({low})} \geq 2.0},} & (I) \\ {{8.0 \geq \frac{{MFR}({high})}{{MFR}({low})} \geq 2.5},} & ({Ia}) \\ {{5.0 \geq \frac{{MFR}({high})}{{MFR}({low})} \geq 3.5},} & ({Ib}) \end{matrix}$ wherein MFR (high) is the melt flow rate MFR₂ (230° C./2.16 kg) [g/10 min] of the propylene homopolymer fraction with the higher melt flow rate MFR₂ (230° C./2.16 kg) and MFR (low) is the melt flow rate MFR₂ (230° C./2.16 kg) [g/10 min] of the propylene homopolymer fraction with the lower melt flow rate MFR₂ (230° C./2.16 kg).

Preferably, the first propylene copolymer fraction (H-PP1) is the random copolymer fraction with the higher melt flow rate MFR₂ (230° C./2.16 kg) and the second propylene copolymer fraction (H-PP2) is the random copolymer fraction with the lower melt flow rate MFR₂ (230° C./2.16 kg).

Accordingly, it is preferred that the first propylene homopolymer fraction (H-PP1) has a melt flow rate MFR₂ (230° C./2.16 kg) in the range of 90 to 160 g/10 min, more preferably in the range of 100 to 150 g/10 min, still more preferably in the range of 120 to 140 g/10 min and/or that the second propylene copolymer fraction (EC2) has a melt flow rate MFR₂ (230° C./2.16 kg) in the range of 10 to 39 g/10 min, more preferably in the range of 17 to 32 g/10 min, still more preferably in the range of 22 to 27 g/10 min.

Further, the weight ratio between the first propylene homopolymer fraction (H-PP1) and second propylene homopolymer fraction (H-PP2) preferably is 20:80 to 80:20, more preferably 75:25 to 25:75, still more preferably 55:45 to 45:55.

The second heterophasic propylene copolymer (HECO2) preferably comprises 60 to 95 wt.-%, more preferably 70 to 90 wt.-%, still more preferably 72 to 87 wt.-% of the second propylene polymer (M2), based on the total weight of the second heterophasic propylene copolymer (HECO2).

Additionally, the second heterophasic propylene copolymer (HECO2) preferably comprises 5 to 40 wt.-%, more preferably 10 to 30 wt.-%, still more preferably 13 to 28 wt.-% of the second elastomeric propylene copolymer (E2), based on the total weight of the second heterophasic propylene copolymer (HECO2).

Thus, it is appreciated that the second heterophasic propylene copolymer (HECO2) preferably comprises, more preferably consists of, 60 to 95 wt.-%, more preferably 70 to 90 wt.-%, still more preferably 72 to 87 wt.-% of the second propylene polymer (M2) and 5 to 40 wt.-%, more preferably 10 to 30 wt.-%, still more preferably 13 to 28 wt.-% of the second elastomeric propylene copolymer (E2), based on the total weight of the second heterophasic propylene copolymer (HECO2).

Accordingly, a further component of the second heterophasic propylene copolymer (HECO2) is the second elastomeric propylene copolymer (E2) dispersed in the matrix (M) being the second propylene polymer (M2). Concerning the comonomers used in the second elastomeric propylene copolymer (E2) it is referred to the information provided for the first heterophasic propylene copolymer (HECO1). Accordingly, the second elastomeric propylene copolymer (E2) comprises monomers copolymerizable with propylene, for example comonomers such as ethylene and/or C₄ to C₈ α-olefins, in particular ethylene and/or C₄ to C₆ α-olefins, e.g. 1-butene and/or 1-hexene. Preferably, the second elastomeric propylene copolymer (E2) comprises, especially consists of, monomers copolymerizable with propylene from the group consisting of ethylene, 1-butene and 1-hexene. More specifically, the second elastomeric propylene copolymer (E2) comprises—apart from propylene—units derivable from ethylene and/or 1-butene. Thus, in an especially preferred embodiment the second elastomeric propylene copolymer (E2) comprises units derivable from ethylene and propylene only.

The comonomer content of the second elastomeric propylene copolymer (E2) preferably is in the range of 15.0 to 55.0 mol-%, more preferably in the range of 20.0 to 50.0 mol-%, still more preferably in the range of 25.0 to 40.0 mol-%.

The second heterophasic propylene copolymer (HECO2) as defined in the instant invention may contain up to 5.0 wt.-% additives, like nucleating agents and antioxidants, as well as slip agents and antiblocking agents. Preferably the additive content (without α-nucleating agents) is below 3.0 wt.-%, like below 1.0 wt.-%.

According to a preferred embodiment of the present invention, the second heterophasic propylene copolymer (HECO2) contains an α-nucleating agent.

Regarding the preferred α-nucleating agents, reference is made to the α-nucleating agents described above with regard to the first heterophasic propylene copolymer (HECO1).

The second heterophasic propylene copolymer (HECO2) can be produced by blending the second propylene polymer (M2) and the second elastomeric propylene copolymer (E2). However, it is preferred that the second heterophasic propylene copolymer (HECO2) is produced in a sequential step process, using reactors in serial configuration and operating at different reaction conditions. As a consequence, each fraction prepared in a specific reactor may have its own molecular weight distribution and/or comonomer content distribution.

Accordingly, it is preferred that the second heterophasic propylene copolymer (HECO2) is produced in a sequential polymerization process comprising the steps of

-   (a) polymerizing propylene and optionally at least one ethylene     and/or C₄ to C₁₂ α-olefin in a first reactor (R₁) obtaining the     first polypropylene fraction of the first propylene polymer (M1),     preferably said first polypropylene fraction is a propylene     homopolymer, -   (b) transferring the first polypropylene fraction into a second     reactor (R₂), -   (c) polymerizing in the second reactor (R₂) and in the presence of     said first polypropylene fraction propylene and optionally at least     one ethylene and/or C₄ to C₁₂ α-olefin obtaining thereby the second     polypropylene fraction, preferably said second polypropylene     fraction is a second propylene homopolymer, said first polypropylene     fraction and said second polypropylene fraction form the second     propylene polymer (M2), i.e. the matrix of the second heterophasic     propylene copolymer (HECO2), -   (d) transferring the second propylene polymer (M2) of step (c) into     a third reactor (R₃), -   (e) polymerizing in the third reactor (R₃) and in the presence of     the second propylene polymer (M2) obtained in step (c) propylene and     ethylene to obtain the first propylene copolymer fraction of the     second elastomeric propylene copolymer (E2) dispersed in the second     propylene polymer (M2), -   (f) transferring the second propylene polymer (M2) and the first     propylene copolymer fraction of the second elastomeric propylene     copolymer (E2) into a fourth reactor (R₄), -   (g) polymerizing in the fourth reactor (R₄) and in the presence of     the second propylene polymer (M2) and the first propylene copolymer     fraction of the second elastomeric propylene copolymer (E2)     propylene and ethylene to obtain the second propylene copolymer     fraction of the second elastomeric propylene copolymer (E2)     dispersed in the second propylene polymer (M2), the second propylene     polymer (M2) and the second elastomeric propylene copolymer (E) form     the second propylene copolymer (HECO2).

Of course, in the first reactor (R₁) the second polypropylene fraction can be produced and in the second reactor (R₂) the first polypropylene fraction can be obtained. The same holds true for the elastomeric propylene copolymer phase.

Preferably between the second reactor (R₂) and the third reactor (R₃) the monomers are flashed out.

The term “sequential polymerization process” indicates that the second heterophasic propylene copolymer (HECO2) is produced in at least two, like three or four reactors connected in series. Accordingly, the present process comprises at least a first reactor (R₁) and a second reactor (R₂), more preferably a first reactor (R₁), a second reactor (R₂), a third reactor (R₃) and a fourth reactor (R₄). Regarding the term “polymerization reactor”, reference is made to the definition provided above.

The first reactor (R₁) is preferably a slurry reactor (SR) and can be any continuous or simple stirred batch tank reactor or loop reactor operating in bulk or slurry. Bulk means a polymerization in a reaction medium that comprises of at least 60% (w/w) monomer.

According to the present invention the slurry reactor (SR) is preferably a (bulk) loop reactor (LR).

The second reactor (R₂) can be a slurry reactor, like a loop reactor, as the first reactor or alternatively a gas phase reactor (GPR).

The third reactor (R₃) and the fourth reactor (R₄) are preferably gas phase reactors (GPR).

Such gas phase reactors (GPR) can be any mechanically mixed or fluid bed reactors. Preferably the gas phase reactors (GPR) comprise a mechanically agitated fluid bed reactor with gas velocities of at least 0.2 m/sec. Thus it is appreciated that the gas phase reactor is a fluidized bed type reactor preferably with a mechanical stirrer.

Thus in a preferred embodiment the first reactor (R₁) is a slurry reactor (SR), like a loop reactor (LR), whereas the second reactor (R₂), the third reactor (R₃) and the fourth reactor (R₄) are gas phase reactors (GPR). Accordingly for the instant process at least four, preferably four polymerization reactors, namely a slurry reactor (SR), like a loop reactor (LR), a first gas phase reactor (GPR-1), a second gas phase reactor (GPR-2) and a third gas phase ractor (GPR-3) connected in series are used. If needed prior to the slurry reactor (SR) a pre-polymerization reactor is placed.

In another preferred embodiment the first reactor (R₁) and second reactor (R₂) are slurry reactors (SR), like a loop reactors (LR), whereas the third reactor (R₃) and the fourth reactor (R₄) are gas phase reactors (GPR). Accordingly for the instant process at least three, preferably three polymerization reactors, namely two slurry reactors (SR), like two loop reactors (LR), and two gas phase reactors (GPR-1) and (GPR-2) connected in series are used. If needed prior to the first slurry reactor (SR) a pre-polymerization reactor is placed.

A preferred multistage process is a “loop-gas phase”-process, such as developed by Borealis A/S, Denmark (known as BORSTAR® technology) described e.g. in patent literature, such as in EP 0 887 379, WO 92/12182 WO 2004/000899, WO 2004/111095, WO 99/24478, WO 99/24479 or in WO 00/68315.

A further suitable slurry-gas phase process is the Spheripol® process of Basell.

Preferably, in the instant process for producing the second heterophasic propylene copolymer (HECO2) as defined above the conditions for the first reactor (R₁), i.e. the slurry reactor (SR), like a loop reactor (LR), of step (a) may be as follows:

-   -   the temperature is within the range of 50° C. to 110° C.,         preferably between 60° C. and 100° C., more preferably between         68 and 95° C.,     -   the pressure is within the range of 20 bar to 80 bar, preferably         between 40 bar to 70 bar,     -   hydrogen can be added for controlling the molar mass in a manner         known per se.

Subsequently, the reaction mixture from step (a) is transferred to the second reactor (R₂), i.e. gas phase reactor (GPR-1), i.e. to step (c), whereby the conditions in step (c) are preferably as follows:

-   -   the temperature is within the range of 50° C. to 130° C.,         preferably between 60° C. and 100° C.,     -   the pressure is within the range of 5 bar to 50 bar, preferably         between 15 bar to 35 bar,     -   hydrogen can be added for controlling the molar mass in a manner         known per se.

The residence time can vary in the three reactor zones.

In one embodiment of the process for producing the polypropylene the residence time in bulk reactor, e.g. loop is in the range 0.1 to 2.5 hours, e.g. 0.15 to 1.5 hours and the residence time in gas phase reactor will generally be 0.2 to 6.0 hours, like 0.5 to 4.0 hours.

If desired, the polymerization may be effected in a known manner under supercritical conditions in the first reactor (R₁), i.e. in the slurry reactor (SR), like in the loop reactor (LR), and/or as a condensed mode in the gas phase reactors (GPR).

Preferably the process comprises also a prepolymerization with the catalyst system, as described in detail below, comprising a Ziegler-Natta procatalyst, an external donor and optionally a cocatalyst.

In a preferred embodiment, the prepolymerization is conducted as bulk slurry polymerization in liquid propylene, i.e. the liquid phase mainly comprises propylene, with minor amount of other reactants and optionally inert components dissolved therein.

The prepolymerization reaction is typically conducted at a temperature of 10 to 60° C., preferably from 15 to 50° C., and more preferably from 20 to 45° C.

The pressure in the prepolymerization reactor is not critical but must be sufficiently high to maintain the reaction mixture in liquid phase. Thus, the pressure may be from 20 to 100 bar, for example 30 to 70 bar.

The catalyst components are preferably all introduced to the prepolymerization step. However, where the solid catalyst component (i) and the cocatalyst (ii) can be fed separately it is possible that only a part of the cocatalyst is introduced into the prepolymerization stage and the remaining part into subsequent polymerization stages. Also in such cases it is necessary to introduce so much cocatalyst into the prepolymerization stage that a sufficient polymerization reaction is obtained therein.

It is possible to add other components also to the prepolymerization stage. Thus, hydrogen may be added into the prepolymerization stage to control the molecular weight of the prepolymer as is known in the art. Further, antistatic additive may be used to prevent the particles from adhering to each other or to the walls of the reactor.

The precise control of the prepolymerization conditions and reaction parameters is within the skill of the art.

According to the invention the second heterophasic propylene copolymer (HECO2) is obtained by a multistage polymerization process, as described above, in the presence of a catalyst system comprising as component (i) a Ziegler-Natta procatalyst which contains a trans-esterification product of a lower alcohol and a phthalic ester.

Regarding the preferred catalyst system, reference is made to the catalyst defined above with regard to the first heterophasic propylene copolymer (HECO1).

In a further embodiment, the Ziegler-Natta procatalyst for the production of the second heterophasic propylene copolymer (HECO2) can also be modified by polymerizing a vinyl compound in the presence of the catalyst system as described above.

The Plastomer (PL)

According to a preferred embodiment of the present invention, the polypropylene composition (C) further comprises a plastomer (PL) being a copolymer of ethylene and a C₄ to C₈ α-olefin.

The plastomer (PL) can be any elastomeric polyolefin with the proviso that it chemically differs from the elastomeric propylene copolymers (E1) and (E2) as defined herein. More preferably the plastomer (PL) is a very low density polyolefin, still more preferably a very low density polyolefin polymerized using single site catalysis, preferably metallocene catalysis. Typically, the plastomer (PL) is an ethylene copolymer.

The plastomer (PL) has a density below 0.900 g/cm³. More preferably, the density of the plastomer (PL) is equal or below 0.890 g/cm³, still more preferably in the range of 0.845 to 0.890 g/cm³.

Preferably, the plastomer (PL) has a melt flow rate MFR₂ (190° C., 2.16 kg) of less than 50 g/10 min, more preferably from 10.0 to 40 g/10 min, still more preferably from 15.0 to 35 g/10 min, like a range from 25.0 to 33.0 g/10 min.

Preferably, the plastomer (PL) comprises units derived from ethylene and a C₄ to C₂₀ α-olefin.

The plastomer (PL) comprises, preferably consists of, units derivable from (i) ethylene and (ii) at least another C₄ to C₂₀ α-olefin, like C₄ to C₁₀ α-olefin, more preferably units derivable from (i) ethylene and (ii) at least another α-olefin selected form the group consisting of 1-butene, 1-pentene, 1-hexene, 1-heptene and 1-octene. It is especially preferred that the plastomer (PL) comprises at least units derivable from (i) ethylene and (ii) 1-butene or 1-octene. It is especially preferred that the plastomer (PL) is a copolymer of ethylene and 1-octene.

In an especially preferred embodiment, the plastomer (PL) consists of units derivable from ethylene and 1-octene.

The comonomer content, like the C₄ to C₂₀ α-olefin content, of the plastomer (PL) is in the range of 3.0 to 25.0 mol-%, more preferably in the range of 4.0 to 20.0 mol-%, still more preferably in the range of 5.0 to 15.0 mol-%, like in the range of 6.0 to 10.0 mol-%.

In one preferred embodiment the plastomer (PL) is prepared with at least one metallocene catalyst. The plastomer (PL) may also be prepared with more than one metallocene catalyst or may be a blend of multiple elastomers prepared with different metallocene catalysts. In some embodiments, the plastomer (PL) is a substantially linear ethylene polymer (SLEP). SLEPs and other metallocene catalysed plastomers (PL) are known in the art, for example, U.S. Pat. No. 5,272,236. These resins are also commercially available, for example, as Queo™ plastomers available from Borealis, ENGAGE™ plastomer resins available from Dow Chemical Co. or EXACT™ polymers from Exxon or TAFMER™ polymers from Mitsui.

The High Density Polyethylene (HDPE)

According to a preferred embodiment of the present invention, the polypropylene composition (C) further comprises a high density polyethylene (HDPE).

The expression “high density polyethylene” used in the instant invention relates to a polyethylene obtained in the presence of a Ziegler-Natta or metallocene catalyst that consists substantially, i.e. of more than 99.70 mol-%, still more preferably of at least 99.80 mol-%, of ethylene units. In a preferred embodiment only ethylene units in the high density polyethylene (HDPE) are detectable.

The high density polyethylene (HDPE) has a density of at least 0.800 g/cm³. More preferably, the high density polyethylene (HDPE) has a density in the range of 0.830 to 0.970 g/cm³, still more preferably in the range of 0.900 to 0.965 g/cm³, like in the range of 0.940 to 0.960 g/cm³.

It is especially preferred that the high density polyethylene (HDPE) has a weight average molecular weight Mw in the range of 60 to 85 kg/mol, preferably in the range of 65 to 85 kg/mol, still more preferably in the range of 70 to 80 kg/mol.

Further it is preferred that the high density polyethylene (HDPE) has a rather broad molecular weight distribution (Mw/Mn). Accordingly, it is preferred that the molecular weight distribution (Mw/Mn) of the high density polyethylene (HDPE) is in the range of 6.0 to 8.0, more preferably in the range of 6.5 to 7.5, like in the range of 6.5 to 7.0.

Additionally, it is preferred that the high density polyethylene (HDPE) has a rather high melt flow rate. Accordingly, the melt flow rate (190° C.) measured according to ISO 1133 of the high density polyethylene (HDPE) is preferably in the range of 20 to 40 g/10 min, more preferably in the range of 25 to 35 g/10 min, still more preferably in the range of 27 to 32 g/10 min at 190° C.

Preferably, the high density polyethylene (HDPE) according to the present invention is a high density polyethylene known in the art. In particular, it is preferred that the high density polyethylene (HDPE) is the commercial ethylene homopolymer MG9641 of Borealis AG.

The Inorganic Filler (F)

A further requirement of the composition according to this invention is the presence of an inorganic filler (F).

Preferably the inorganic filler (F) is a mineral filler. It is appreciated that the inorganic filler (F) is a phyllosilicate, mica or wollastonite. Even more preferred the inorganic filler (F) is selected from the group consisting of mica, wollastonite, kaolinite, smectite, montmorillonite and talc.

The most preferred inorganic fillers (F) are talc and/or wollastonite.

It is appreciated that the filler (F) has median particle size (D₅₀) in the range of 0.8 to 20 μM and a top cut particle size (D₉₅) in the range of 10 to 20 μm, preferably a median particle size (D₅₀) in the range of 5.0 to 8.0 μm and top cut particle size (D₉₅) in the range of 12 to 17 μm, more preferably a median particle size (D₅₀) in the range of 5.5 to 7.8 μm and top cut particle size (D₉₅) of 13 to 16.5 μm.

According to this invention the filler (F) does not belong to the class of alpha nucleating agents and additives (AD).

The the filler (F) is state of the art and a commercially available product.

Additives (AD)

In addition the first heterophasic propylene copolymer (HECO1), the second heterophasic propylene copolymer (HECO2), the inorganic filler (F), optionally the plastomer (PL) and optionally the high density polyethylene (HDPE), the composition (C) of the invention may include additives (AD). Typical additives are acid scavengers, antioxidants, colorants, light stabilisers, plasticizers, slip agents, anti-scratch agents, dispersing agents, processing aids, lubricants, pigments, and the like. As indicated above the inorganic filler (F) is not regarded as an additive (AD).

Such additives are commercially available and for example described in “Plastic Additives Handbook”, 6^(th) edition 2009 of Hans Zweifel (pages 1141 to 1190).

Furthermore, the term “additives (AD)” according to the present invention also includes carrier materials, in particular polymeric carrier materials.

The Polymeric Carrier Material

Preferably the composition (C) of the invention does not comprise (a) further polymer (s) different to the first and second heterophasic propylene copolymers (HECO1) and (HECO2), the plastomer (PL) and the high density polyethylene (HDPE), in an amount exceeding 15 wt.-%, preferably in an amount exceeding 10 wt.-%, more preferably in an amount exceeding 9 wt.-%, based on the weight of the composition (C). Any polymer being a carrier material for additives (AD) is not calculated to the amount of polymeric compounds as indicated in the present invention, but to the amount of the respective additive.

The polymeric carrier material of the additives (AD) is a carrier polymer to ensure a uniform distribution in the composition (C) of the invention. The polymeric carrier material is not limited to a particular polymer. The polymeric carrier material may be ethylene homopolymer, ethylene copolymer obtained from ethylene and α-olefin comonomer such as C₃ to C₈ α-olefin comonomer, propylene homopolymer and/or propylene copolymer obtained from propylene and α-olefin comonomer such as ethylene and/or C₄ to C₈ α-olefin comonomer.

The Article

The composition of the present invention is preferably used for the production of articles, more preferably of foamed articles. Even more preferred is the use for the production of automotive articles, especially of car interiors and exteriors, like bumpers, side trims, step assists, body panels, spoilers, dashboards, interior trims and the like.

The current invention also provides articles, more preferably foamed articles, comprising, preferably comprising at least 60 wt.-%, more preferably at least 80 wt.-%, yet more preferably at least 95 wt.-%, like consisting of, the inventive composition. Accordingly, the present invention is especially directed to parts of automotive articles, especially to car interiors and exteriors, like bumpers, side trims, step assists, body panels, spoilers, dashboards, interior trims and the like, comprising, preferably comprising at least 60 wt.-%, more preferably at least 80 wt.-%, yet more preferably at least 95 wt.-%, like consisting of, the inventive composition.

The Use

The present invention is also directed to the use of the inventive composition for the production of a foamed article as described in the previous paragraphs.

The present invention will now be described in further detail by the examples provided below.

EXAMPLES 1. Measuring Methods

The following definitions of terms and determination methods apply for the above general description of the invention as well as to the below examples unless otherwise defined.

Calculation of comonomer content of the elastomeric copolymer fraction, i.e. the polymer fraction produced in the third reactor (R3), of the first heterophasic propylene copolymer (HECO1):

$\begin{matrix} {\frac{{C({PP})} - {{w\left( {{PP}\; 12} \right)} \times {C\left( {{PP}\; 12} \right)}}}{w\left( {{PP}\; 3} \right)} = {C\left( {{PP}\; 3} \right)}} & (I) \end{matrix}$ wherein

-   w(PP12) is the weight fraction [in wt.-%] of the first and second     propylene polymer fraction, i.e. the polymer produced in the first     and second reactor (R1+R2), -   w(PP3) is the weight fraction [in wt.-%] of the elastomeric     propylene copolymer fraction, i.e. the polymer produced in the third     reactor (R3), -   C(PP12) is the comonomer content [in mol-%] of the first and second     propylene polymer fraction, i.e. the polymer produced in the first     and second reactor (R1+R2), -   C(PP) is the comonomer content [in mol-%] of the first propylene     polymer fraction, the second propylene polymer fraction and the     elastomeric propylene copolymer fraction, i.e. polymer produced in     the first, second and third reactor (R1+R2+R3), -   C(PP3) is the calculated comonomer content [in mol-%] of the     elastomeric propylene copolymer fraction, i.e. the polymer produced     in the third reactor (R3).

Calculation of the xylene cold soluble (XCS) content of the elastomeric propylene copolymer fraction, i.e. the polymer fraction produced in the third reactor (R3), of the first heterophasic propylene copolymer (HECO1):

$\begin{matrix} {\frac{{{XS}({HECO})} - {{w\left( {{PP}\; 12} \right)} \times {{XS}\left( {{PP}\; 12} \right)}}}{w(E)} = {{XS}(E)}} & ({II}) \end{matrix}$ wherein

-   w(PP12) is the weight fraction [in wt.-%] of the first and second     propylene polymer fraction, i.e. the polymer produced in the first     and second reactor (R1+R2), -   w(E) is the weight fraction [in wt.-%] of the elastomeric propylene     copolymer fraction, i.e. the polymer produced in the third reactor     (R3) -   XS(PP12) is the xylene cold soluble (XCS) content [in wt.-%] of the     first and second propylene polymer fraction, i.e. the polymer     produced in the first and second reactor (R1+R2), -   XS(HECO) is the xylene cold soluble (XCS) content [in wt.-%] of the     first propylene polymer fraction, the second propylene polymer     fraction and the elastomeric propylene copolymer fraction, i.e.     polymer produced in the first, second reactor and third reactor     (R1+R2+R3), -   XS(E) is the calculated xylene cold soluble (XCS) content [in wt.-%]     of the elastomeric propylene copolymer fraction, i.e. the polymer     produced in the second and third reactor (R2+3).

Calculation of melt flow rate MFR₂ (230° C.) of the elastomeric propylene copolymer fraction, i.e. the polymer fraction produced in the third reactor (R3), of the first heterophasic propylene copolymer (HECO1):

$\begin{matrix} {{{MFR}\left( {{PP}\; 3} \right)} = 10^{\lbrack\frac{{\log{({{MFR}{({PP})}})}} - {{w{({{PP}\; 12})}} \times {\log{({{MFR}{({{PP}\; 12})}})}}}}{w{({{PP}\; 3})}}\rbrack}} & ({III}) \end{matrix}$ wherein

-   w(PP12) is the weight fraction [in wt.-%] of the first and second     propylene polymer fractions, i.e. the polymer produced in the first     and second reactor (R1+R2), -   w(PP3) is the weight fraction [in wt.-%] of the elastomeric     propylene copolymer fraction, i.e. the polymer produced in the third     reactor (R3), -   MFR(PP12) is the melt flow rate MFR₂ (230° C.) [in g/10 min] of the     first and second propylene fractions, i.e. the polymer produced in     the first and second reactor (R1+R2), -   MFR(PP) is the melt flow rate MFR₂ (230° C.) [in g/10 min] of the     first and second propylene polymer fractions and the elastomeric     propylene copolymer fraction, i.e. the polymer produced in the     first, second and third reactor (R1+R2+R3), -   MFR(PP3) is the calculated melt flow rate MFR₂ (230° C.) [in g/10     min] of the elastomeric propylene copolymer fraction, i.e. the     polymer produced in the third reactor (R3).

Calculation of comonomer content of the elastomeric propylene copolymer fraction, i.e. the polymer fraction produced in the third reactor (R3), of the first heterophasic propylene copolymer (HECO1):

$\begin{matrix} {\frac{{C({HECO})} - {{w({PP})} \times {C({PP})}}}{w(E)} = {C(E)}} & ({IV}) \end{matrix}$ wherein

-   w(PP) is the weight fraction [in wt.-%] of the first and second     propylene polymer fractions, i.e. the polymer produced in the first     and second reactor (R1+R2), -   w(E) is the weight fraction [in wt.-%] of the elastomeric propylene     copolymer, i.e. of the polymer produced in the third reactor (R3), -   C(PP) is the comonomer content [in mol-%] of the first and second     propylene polymer fractions, i.e. the polymer produced in the first     and second reactor (R1+R2), -   C(HECO) is the comonomer content [in mol-%] of the propylene     copolymer, i.e. is the comonomer content [in mol-%] of the polymer     obtained after polymerization in the third reactor (R3), -   C(E) is the calculated comonomer content [in mol-%] of the     elastomeric propylene copolymer fraction, i.e. of the polymer     produced in the third reactor (R3).

Calculation of comonomer content of the first elastomeric propylene copolymer fraction, i.e. the polymer fraction produced in the third reactor (R3), of the second heterophasic propylene copolymer (HECO2):

$\begin{matrix} {\frac{{C({PP})} - {{w\left( {{PP}\; 12} \right)} \times {C\left( {{PP}\; 12} \right)}}}{w\left( {{PP}\; 3} \right)} = {C\left( {{PP}\; 3} \right)}} & (V) \end{matrix}$ wherein

-   w(PP12) is the weight fraction [in wt.-%] of the first and second     propylene polymer fractions, i.e. the polymer produced in the first     and second reactor (R1+R2), -   w(PP3) is the weight fraction [in wt.-%] of the first elastomeric     propylene copolymer fraction, i.e. the polymer produced in the third     reactor (R3), -   C(PP12) is the comonomer content [in mol-%] of the first and second     propylene polymer fractions, i.e. the polymer produced in the first     and second reactor (R1+R2), -   C(PP) is the comonomer content [in mol-%] of the first and second     propylene polymer fractions and the first elastomeric propylene     copolymer fraction, i.e. the polymer produced in the first, second     and third reactor (R1+R2+R3), -   C(PP2) is the calculated comonomer content [in mol-%] of the first     elastomeric propylene copolymer fraction, i.e. the polymer produced     in the third reactor (R3).

Calculation of comonomer content of the second elastomeric propylene copolymer fraction, i.e. the polymer fraction produced in the fourth reactor (R3), of the second heterophasic propylene copolymer (HECO2):

$\begin{matrix} {\frac{{C({PP})} - {{w\left( {{PP}\; 123} \right)} \times {C\left( {{PP}\; 123} \right)}}}{w\left( {{PP}\; 4} \right)} = {C\left( {{PP}\; 4} \right)}} & ({VI}) \end{matrix}$ wherein

-   w(PP123) is the weight fraction [in wt.-%] of the first and second     propylene polymer fractions and the first elastomeric propylene     copolymer fraction, i.e. the polymer produced in the first, second     and third reactor (R1+R2+R3), -   w(PP4) is the weight fraction [in wt.-%] of second elastomeric     propylene copolymer fraction, i.e. the polymer produced in the     fourth reactor (R4), -   C(PP123) is the comonomer content [in mol-%] of the first and second     propylene polymer fractions and the first elastomeric propylene     copolymer fraction, i.e. the polymer produced in the first, second     and third reactor (R1+R2+R3), -   C(PP) is the comonomer content [in mol-%] of the first and second     propylene polymer fractions and the first and second elastomeric     propylene copolymer fractions, i.e. the polymer produced in the     first, second, third and fourth reactor (R1+R2+R3), -   C(PP4) is the calculated comonomer content [in mol-%] of the second     elastomeric propylene copolymer fraction, i.e. the polymer produced     in the fourth reactor (R4).

Calculation of the xylene cold soluble (XCS) content of the elastomeric propylene copolymer fraction, i.e. the polymer fraction produced in the third and fourth reactor (R3+R4), of the second heterophasic propylene copolymer (HECO2):

$\begin{matrix} {\frac{{{XS}({HECO})} - {{w\left( {{PP}\; 12} \right)} \times {{XS}\left( {{PP}\; 12} \right)}}}{w(E)} = {{XS}(E)}} & ({VII}) \end{matrix}$ wherein

-   w(PP12) is the weight fraction [in wt.-%] of the first and second     propylene polymer fractions, i.e. the polymer produced in the first     and second reactor (R1+R2), -   w(E) is the weight fraction [in wt.-%] of the elastomeric propylene     copolymer fraction, i.e. the polymer produced in the third and     fourth reactor (R3+R4) -   XS(PP12) is the xylene cold soluble (XCS) content [in wt.-%] of the     first and second propylene polymer fractions, i.e. the polymer     produced in the first and second reactor (R1+R2), -   XS(HECO) is the xylene cold soluble (XCS) content [in wt.-%] of the     first and second propylene polymer fractions and the elastomeric     propylene copolymer fraction, i.e. polymer produced in the first,     second, third and fourth (R1+R2+R3+R4), -   XS(E) is the calculated xylene cold soluble (XCS) content [in wt.-%]     of the elastomeric propylene copolymer fraction, i.e. the polymer     produced in the third and fourth reactor (R3+R4).

Calculation of the xylene cold soluble (XCS) content of the first elastomeric propylene copolymer fraction, i.e. the polymer fraction produced in the third reactor (R3), of the second heterophasic propylene copolymer (HECO2):

$\begin{matrix} {\frac{{{XS}({PP})} - {{w\left( {{PP}\; 12} \right)} \times {{XS}\left( {{PP}\; 12} \right)}}}{w\left( {{PP}\; 3} \right)} = {{XS}\left( {{PP}\; 3} \right)}} & ({VIII}) \end{matrix}$ wherein

-   w(PP12) is the weight fraction [in wt.-%] of the first and second     propylene polymer fractions, i.e. the polymer produced in the first     and second reactor (R1+R2), -   w(PP3) is the weight fraction [in wt.-%] of the first elastomeric     propylene copolymer fraction, i.e. the polymer produced in the third     reactor (R3) -   XS(PP12) is the xylene cold soluble (XCS) content [in wt.-%] of the     first and second elastomeric propylene polymer fractions, i.e. the     polymer produced in the first and second reactor (R1+R2), -   XS(PP) is the xylene cold soluble (XCS) content [in wt.-%] of the     first and second propylene polymer fraction and the first     elastomeric propylene copolymer fraction, i.e. polymer produced in     the first, second and third reactor (R1+R2+R3), -   XS(PP3) is the calculated xylene cold soluble (XCS) content [in     wt.-%] of the first elastomeric propylene copolymer fraction, i.e.     the polymer produced in the third reactor (R3).

Calculation of the xylene cold soluble (XCS) content of the second elastomeric propylene copolymer fraction, i.e. the polymer fraction produced in the fourth reactor (R4):

$\begin{matrix} {\frac{{{XS}({PP})} - {{w\left( {{PP}\; 123} \right)} \times {{XS}\left( {{PP}\; 123} \right)}}}{w\left( {{PP}\; 4} \right)} = {{XS}\left( {{PP}\; 4} \right)}} & ({IX}) \end{matrix}$ wherein

-   w(PP123) is the weight fraction [in wt.-%] of the first and second     propylene polymer fractions and the first elastomeric propylene     copolymer fraction, i.e. the polymer produced in the first, second     and third reactor (R1+R2+R3), -   w(PP4) is the weight fraction [in wt.-%] of the second propylene     copolymer fraction, i.e. the polymer produced in the fourth reactor     (R4) -   XS(PP123) is the xylene cold soluble (XCS) content [in wt.-%] of the     first and second propylene polymer fractions and the first     elastomeric propylene copolymer fraction, i.e. the polymer produced     in the first, second and third reactor (R1+R2+R3), -   XS(PP) is the xylene cold soluble (XCS) content [in wt.-%] of the     first and second propylene polymer fractions and the first and     second elastomeric propylene copolymer fractions, i.e. polymer     produced in the first, second reactor and third reactor     (R1+R2+R3+R4), -   XS(PP4) is the calculated xylene cold soluble (XCS) content [in     wt.-%] of the second elastomeric propylene copolymer fraction, i.e.     the polymer produced in the fourth reactor (R4).

Calculation of melt flow rate MFR₂ (230° C.) of the second propylene polymer fraction, i.e. the polymer fraction produced in the second reactor (R2), of the second heterophasic propylene copolymer (HECO2):

$\begin{matrix} {{{MFR}\left( {{PP}\; 2} \right)} = 10^{\lbrack\frac{{\log{({{MFR}{({PP})}})}} - {{w{({{PP}\; 1})}} \times {\log{({{MFR}{({{PP}\; 1})}})}}}}{w{({{PP}\; 2})}}\rbrack}} & (X) \end{matrix}$ wherein

-   w(PP1) is the weight fraction [in wt.-%] of the first propylene     polymer fraction, i.e. the polymer produced in the first reactor     (R1), -   w(PP2) is the weight fraction [in wt.-%] of the first second     propylene polymer fraction, i.e. the polymer produced in the second     reactor (R2), -   MFR(PP1) is the melt flow rate MFR₂ (230° C.) [in g/10 min] of the     first propylene polymer fraction, i.e. the polymer produced in the     first reactor (R1), -   MFR(PP) is the melt flow rate MFR₂ (230° C.) [in g/10 min] of the     first and second propylene polymer fractions, i.e. the polymer     produced in the first and second reactor (R1+R2), -   MFR(PP2) is the calculated melt flow rate MFR₂ (230° C.) [in g/10     min] of the first propylene polymer fraction, i.e. the polymer     produced in the second reactor (R2).

Calculation of the intrinsic viscosity of the xylene soluble fraction of the first elastomeric propylene copolymer fraction, i.e. the polymer fraction produced in the third reactor (R3), of the second heterophasic propylene copolymer (HECO2):

$\begin{matrix} {\frac{{{IV}({PP})} - {{{XCS}\left( {{PP}\; 12} \right)} \times {{IV}\left( {{PP}\; 12} \right)}}}{{XCS}\left( {{PP}\; 3} \right)} = {{IV}\left( {{PP}\; 3} \right)}} & ({XI}) \end{matrix}$ wherein

-   XCS(PP12) is the xylene soluble fraction [in wt.-%] of the first and     second propylene polymer fractions, i.e. the polymer produced in the     first and second reactor (R1+R2), -   XCS(PP3) is the xylene soluble fraction [in wt.-%] of the first     elastomeric propylene copolymer fraction, i.e. the polymer produced     in the third reactor (R3), -   IV(PP12) is the intrinsic viscosity [in dl/g] of the xylene soluble     fraction of the first and second propylene polymer fractions, i.e.     the polymer produced in the first and second reactor (R1+R2), -   IV(PP) is the intrinsic viscosity [in dl/g] of the xylene soluble     fraction of the first and second propylene polymer fractions and the     first elastomeric propylene copolymer fraction, i.e. polymer     produced in the first, second and third reactor (R1+R2+R3), -   IV(PP3) is the calculated intrinsic viscosity [in dl/g] of the     xylene soluble fraction of the first elastomeric propylene copolymer     fraction, i.e. the polymer produced in the third reactor (R3).

Calculation of the intrinsic viscosity of the xylene soluble fraction of the second elastomeric propylene copolymer fraction, i.e. the polymer fraction produced in the fourth reactor (R4), of the second heterophasic propylene copolymer (HECO2):

$\begin{matrix} {\frac{{{IV}({PP})} - {{{XCS}\left( {{PP}\; 123} \right)} \times {{IV}\left( {{PP}\; 123} \right)}}}{{XCS}\left( {{PP}\; 4} \right)} = {{IV}\left( {{PP}\; 4} \right)}} & ({XII}) \end{matrix}$ wherein

-   XCS(PP123) is the xylene soluble fraction [in wt.-%] of the first     and second propylene polymer fractions and the first elastomeric     propylene copolymer fraction, i.e. the polymer produced in the     first, second and third reactor (R1+R2+R3), -   XCS(PP4) is the xylene soluble fraction [in wt.-%] of second     elastomeric propylene copolymer fraction, i.e. the polymer produced     in the fourth reactor (R4), -   IV(PP123) is the intrinsic viscosity [in dl/g] of the xylene soluble     fraction of the first and second propylene polymer fractions and the     first elastomeric propylene copolymer fraction, i.e. the polymer     produced in the first, second and third reactor (R1+R2+R3), -   IV(PP) is the intrinsic viscosity [in dl/g] of the xylene soluble     fraction of the first and second propylene polymer fractions and the     first and second elastomeric propylene copolymer fractions, i.e.     polymer produced in the first, second, third and fourth reactor     (R1+R2+R3+R4), -   IV(PP4) is the calculated intrinsic viscosity [in dl/g] of the     xylene soluble fraction of the second elastomeric propylene     copolymer fraction, i.e. the polymer produced in the fourth reactor     (R4).

Calculation of comonomer content of the elastomeric propylene copolymer fraction, i.e. the polymer fraction produced in the third and fourth reactor (R3+R4), of the second heterophasic propylene copolymer (HECO2):

$\begin{matrix} {\frac{{C({HECO})} - {{w\left( {{PP}\; 12} \right)} \times {C\left( {{PP}\; 12} \right)}}}{w(E)} = {C(E)}} & ({XIII}) \end{matrix}$ wherein

-   w(PP12) is the weight fraction [in wt.-%] of the first and second     propylene polymer fractions, i.e. the polymer produced in the first     and second reactor (R1+R2), -   w(E) is the weight fraction [in wt.-%] of the elastomeric propylene     copolymer fraction, i.e. the polymer produced in the third and     fourth reactor (R3+R4) -   C(PP12) is the comonomer content [in mol-%] of the first and second     propylene polymer fractions, i.e. the polymer produced in the first     and second reactor (R1+R2), -   C(HECO) is the comonomer content [in mol-%] of the first and second     propylene polymer fractions and the elastomeric propylene copolymer,     i.e. polymer produced in the first, second, third and fourth     (R1+R2+R3+R4), -   C(E) is the calculated comonomer content [in mol-%] of the     elastomeric propylene copolymer fraction, i.e. the polymer produced     in the third and fourth reactor (R3+R4). -   MFR₂ (230° C.) is measured according to ISO 1133 (230° C., 2.16 kg     load). -   MFR₂ (190° C.) is measured according to ISO 1133 (190° C., 2.16 kg     load).

Quantification of Microstructure by NMR Spectroscopy

Quantitative nuclear-magnetic resonance (NMR) spectroscopy was used to quantify the comonomer content and comonomer sequence distribution of the polymers. Quantitative ¹³C {¹H} NMR spectra were recorded in the solution-state using a Bruker Advance III 400 NMR spectrometer operating at 400.15 and 100.62 MHz for ¹H and ¹³C respectively. All spectra were recorded using a ¹³C optimised 10 mm extended temperature probehead at 125° C. using nitrogen gas for all pneumatics. Approximately 200 mg of material was dissolved in 3 ml of 1,2-tetrachloroethane-d₂ (TCE-d₂) along with chromium-(III)-acetylacetonate (Cr(acac)₃) resulting in a 65 mM solution of relaxation agent in solvent (Singh, G., Kothari, A., Gupta, V., Polymer Testing 28 5 (2009), 475). To ensure a homogenous solution, after initial sample preparation in a heat block, the NMR tube was further heated in a rotatary oven for at least 1 hour. Upon insertion into the magnet the tube was spun at 10 Hz. This setup was chosen primarily for the high resolution and quantitatively needed for accurate ethylene content quantification. Standard single-pulse excitation was employed without NOE, using an optimised tip angle, 1 s recycle delay and a bi-level WALTZ16 decoupling scheme (Zhou, Z., Kuemmerle, R., Qiu, X., Redwine, D., Cong, R., Taha, A., Baugh, D. Winniford, B., J. Mag. Reson. 187 (2007) 225; Busico, V., Carbonniere, P., Cipullo, R., Pellecchia, R., Severn, J., Talarico, G., Macromol. Rapid Commun. 2007, 28, 1128). A total of 6144 (6 k) transients were acquired per spectra. Quantitative ¹³C {¹H} NMR spectra were processed, integrated and relevant quantitative properties determined from the integrals using proprietary computer programs. All chemical shifts were indirectly referenced to the central methylene group of the ethylene block (EEE) at 30.00 ppm using the chemical shift of the solvent. This approach allowed comparable referencing even when this structural unit was not present. Characteristic signals corresponding to the incorporation of ethylene were observed Cheng, H. N., Macromolecules 17 (1984), 1950).

For polypropylene homopolymers all chemical shifts are internally referenced to the methyl isotactic pentad (mmmm) at 21.85 ppm.

Characteristic signals corresponding to regio defects (Resconi, L., Cavallo, L., Fait, A., Piemontesi, F., Chem. Rev. 2000, 100, 1253; Wang, W-J., Zhu, S., Macromolecules 33 (2000), 1157; Cheng, H. N., Macromolecules 17 (1984), 1950) or comonomer were observed.

The tacticity distribution was quantified through integration of the methyl region between 23.6-19.7 ppm correcting for any sites not related to the stereo sequences of interest (Busico, V., Cipullo, R., Prog. Polym. Sci. 26 (2001) 443; Busico, V., Cipullo, R., Monaco, G., Vacatello, M., Segre, A. L., Macromolecules 30 (1997) 6251).

Specifically the influence of regio defects and comonomer on the quantification of the tacticity distribution was corrected for by subtraction of representative regio defect and comonomer integrals from the specific integral regions of the stereo sequences.

The isotacticity was determined at the pentad level and reported as the percentage of isotactic pentad (mmmm) sequences with respect to all pentad sequences: [mmmm]%=100*(mmmm/sum of all pentads)

The presence of 2,1 erythro regio defects was indicated by the presence of the two methyl sites at 17.7 and 17.2 ppm and confirmed by other characteristic sites.

Characteristic signals corresponding to other types of regio defects were not observed (Resconi, L., Cavallo, L., Fait, A., Piemontesi, F., Chem. Rev. 2000, 100, 1253).

The amount of 2,1 erythro regio defects was quantified using the average integral of the two characteristic methyl sites at 17.7 and 17.2 ppm: P _(21e) =I _(e6) +I _(e8))/2

The amount of 1,2 primary inserted propene was quantified based on the methyl region with correction undertaken for sites included in this region not related to primary insertion and for primary insertion sites excluded from this region: P ₁₂ =I _(CH3) +P _(12e)

The total amount of propene was quantified as the sum of primary inserted propene and all other present regio defects: P _(total) =P ₁₂ +P _(21e)

The mole percent of 2,1 erythro regio defects was quantified with respect to all propene: [21e] mol %=100*(P _(21e) /P _(total))

For copolymers characteristic signals corresponding to the incorporation of ethylene were observed (Cheng, H. N., Macromolecules 17 (1984), 1950).

With regio defects also observed (Resconi, L., Cavallo, L., Fait, A., Piemontesi, F., Chem. Rev. 2000, 100, 1253; Wang, W-J., Zhu, S., Macromolecules 33 (2000), 1157; Cheng, H. N., Macromolecules 17 (1984), 1950) correction for the influence of such defects on the comonomer content was required.

The comonomer fraction was quantified using the method of Wang et. al. (Wang, W-J., Zhu, S., Macromolecules 33 (2000), 1157) through integration of multiple signals across the whole spectral region in the ¹³C {¹H} spectra. This method was chosen for its robust nature and ability to account for the presence of regio-defects when needed. Integral regions were slightly adjusted to increase applicability across the whole range of encountered comonomer contents.

For systems where only isolated ethylene in PPEPP sequences was observed the method of Wang et. al. was modified to reduce the influence of non-zero integrals of sites that are known to not be present. This approach reduced the overestimation of ethylene content for such systems and was achieved by reduction of the number of sites used to determine the absolute ethylene content to: E=0.5(Sββ+Sβγ+Sβδ+0.5(Sαβ+Sαγ)) Through the use of this set of sites the corresponding integral equation becomes: E=0.5(I _(H) +I _(G)+0.5(I _(C) +I _(D))) using the same notation used in the article of Wang et. al. (Wang, W-J., Zhu, S., Macromolecules 33 (2000), 1157). Equations used for absolute propylene content were not modified.

The mole percent comonomer incorporation was calculated from the mole fraction: E[mol %]=100*fE

The weight percent comonomer incorporation was calculated from the mole fraction: E[wt %]=100*(fE*28.06)/((fE*28.06)+((1−fE)*42.08)) The comonomer sequence distribution at the triad level was determined using the analysis method of Kakugo et al. (Kakugo, M., Naito, Y., Mizunuma, K., Miyatake, T. Macromolecules 15 (1982) 1150). This method was chosen for its robust nature and integration regions slightly adjusted to increase applicability to a wider range of comonomer contents.

Number Average Molecular Weight (M_(n)), Weight Average Molecular Weight (M_(w)) and Molecular Weight Distribution (MWD) Molecular weight averages (Mw, Mn), and the molecular weight distribution (MWD), i.e. the Mw/Mn (wherein Mn is the number average molecular weight and Mw is the weight average molecular weight), were determined by Gel Permeation Chromatography (GPC) according to ISO 16014-4:2003 and ASTM D 6474-99. A PolymerChar GPC instrument, equipped with infrared (IR) detector was used with 3× Olexis and 1× Olexis Guard columns from Polymer Laboratories and 1,2,4-trichlorobenzene (TCB, stabilized with 250 mg/L 2,6-Di tert butyl-4-methyl-phenol) as solvent at 160° C. and at a constant flow rate of 1 mL/min 200 μL. of sample solution were injected per analysis. The column set was calibrated using universal calibration (according to ISO 16014-2:2003) with at least 15 narrow MWD polystyrene (PS) standards in the range of 0.5 kg/mol to 11 500 kg/mol. Mark Houwink constants for PS, PE and PP used are as described per ASTM D 6474-99. All samples were prepared by dissolving 5.0-9.0 mg of polymer in 8 mL (at 160° C.) of stabilized TCB (same as mobile phase) for 2.5 hours for PP or 3 hours for PE at max. 160° C. under continuous gentle shaking in the autosampler of the GPC instrument. DSC analysis, melting temperature (Tm). crystallization temperature (Tc): measured with a TA Instrument Q2000 differential scanning calorimeter (DSC) on 5 to 7 mg samples. DSC run according to ISO 11357/part 3/method C2 in a heat/cool/heat cycle with a scan rate of 10° C./min in the temperature range of −30 to +230° C. Crystallization temperature was determined from the cooling step, while melting temperature was determined from the heating scan.

Intrinsic viscosity is measured according to DIN ISO 1628/1, October 1999 (in Decalin at 135° C.).

Density is measured according to ISO 1183-187. Sample preparation is done by compression moulding in accordance with ISO 1872-2:2007.

The xylene solubles (XCS, wt.-%): Content of xylene cold solubles (XCS) is determined at 25° C. according ISO 16152; first edition; 2005-07-01. The part which remains insoluble is the xylene cold insoluble (XCI) fraction.

Flexural Modulus: The flexural modulus was determined in 3-point-bending according to ISO 178 on 80×10×4 mm³ test bars injection molded at 23° C. in line with EN ISO 1873-2.

Charpy notched impact test: The charpy notched impact strength (Charpy NIS) was measured according to ISO 179 2C/DIN 53453 at 23° C. and −20° C., using injection molded bar test specimens of 80×10×4 mm prepared in accordance with ISO 294-1:1996

Shrinkage in flow and shrinkage cross flow were determined on film gate injection moulded plaques: One is a sector (radius 300 mm and opening angle of 20°) and the other one a stripe (340×65 mm). The two specimens are injection moulded at the same time in different thicknesses and back pressures (2 mm and 300, 400, 500 bars; 2.8 mm and 300, 400, 500 bars; 3.5 mm and 300, 400, 500 bars). The melt temperature is 240° C. and the temperature of the tool 25° C. Average flow front velocity is 3.0±0.2 mm/s for the 2 mm tool, 3.5±0.2 mm/s for the 2.8 mm tool and .0±0.2 mm/s for the 3.5 mm tool.

After the injection moulding process the shrinkage of the specimens is measured at 23° C. and 50% humidity. The measurement intervals are 1, 4, 24, 48 and 96 hours after the injection moulding. To determine the shrinkage 83 and 71 measurement points (generated by eroded dots on the tool surface) of the sector and the stripe, respectively, are recorded with a robot. Both, in flow and cross flow shrinkage of the 2.8 mm thick plates exposed to a back pressure of 400 bars at 96 hours after the injection moulding process are reported as final results.

Surface Appearance of Compact and Foamed Parts

The tendency to show flow marks was examined with a method as described below. This method is described in detail in WO 2010/149529, which is incorporated herein in its entirety.

An optical measurement system, as described by Sybille Frank et al. in PPS 25 Intern. Conf. Polym. Proc. Soc 2009 or Proceedings of the SPIE, Volume 6831, pp 68130T-68130T-8 (2008) was used for characterizing the surface quality.

This method consists of two aspects:

1. Image Recording:

The basic principle of the measurement system is to illuminate the plates with a defined light source (LED) in a closed environment and to record an image with a CCD-camera system.

A schematic setup is given in FIG. 1.

2. Image Analysis:

The specimen is floodlit from one side and the upwards reflected portion of the light is deflected via two mirrors to a CCD-sensor. The such created grey value image is analyzed in lines. From the recorded deviations of grey values the mean square error average (MSEaverage) or mean square error maximum (MSEmax) values are calculated allowing a quantification of surface quality/homogeneity, i.e. the higher the MSE value the more pronounced is the surface defect. MSEaverage and MSEmax values are not comparable. Generally, for one and the same material, the tendency to flow marks increases when the injection speed is increased.

The MSEaverage values were collected on compact injection-moulded plaques 440×148×2.8 mm produced with grain G1. The plaques were injection-moulded with different filling times of 1.5, 3 and 6 sec respectively.

Further Conditions:

Melt temperature: 240° C.

Mould temperature 30° C.

Dynamic pressure: 10 bar hydraulic

The MSEmax values were collected on compact and foamed injection-moulded plaques 210×148×2 mm produced with a one-point gating system and a grain marked here as G2, which differs from G1. The plaques were injection-moulded with filling time of 0.8 s. Hydrocerol ITP 825 from Clariant, with a decomposition temperature of 200° C. was used as a chemical blowing agent. The blowing agent was added during the conversion step in a form of a masterbatch, which contains 40% of active substance defined as a citric acid [www.clariant.com].

Cell structure of the foamed parts was determined by light microscopy from a cross-section of the foamed injection-molded plate.

Maximum force at break was determined on plaques with dimensions 148×148×2 mm during instrumented falling weight impact testing according to ISO 6603-2. The test was performed at room temperature with a lubricated tup with a diameter of 20 mm and impact velocity of 10 mm/s. The maximum force at break was determined as the maximum peak at the force-deformation curve collected during the test.

Compression test was performed on 10×10×2 mm plaques at room temperature according to ISO 604: 2002. The tests were carried out on a Zwick Z010U machine with a test speed of 0.87 mm/min at room temperature. The compressive stress was determined at 1 mm deformation. Thus, the compressive stress is defined as the force at break at 1 mm deformation divided by the specimen area at the beginning of the experiment.

2. Examples

Preparation of the Catalyst for HECO1, HECO2 and HECO2a

First, 0.1 mol of MgCl2×3 EtOH was suspended under inert conditions in 250 ml of decane in a reactor at atmospheric pressure. The solution was cooled to the temperature of −15° C. 5 and 300 ml of cold TiCl4 was added while maintaining the temperature at said level. Then, the temperature of the slurry was increased slowly to 20° C. At this temperature, 0.02 mol of dioctylphthalate (DOP) was added to the slurry. After the addition of the phthalate, the temperature was raised to 135° C. during 90 minutes and the slurry was allowed to stand for 60 minutes. Then, another 300 ml of TiCl4 was added and the temperature was kept at 135° C. 10 for 120 minutes. After this, the catalyst was filtered from the liquid and washed six times with 300 ml heptane at 80° C. Then, the solid catalyst component was filtered and dried. Catalyst and its preparation concept is described in general e.g. in patent publications EP 491566, EP 591224 and EP 586390.

The catalyst was further modified (VCH modification of the catalyst). 35 ml of mineral oil (Paraffinum Liquidum PL68) was added to a 125 ml stainless steel reactor followed by 0.82 g of triethyl aluminium (TEAL) and 0.33 g of dicyclopentyl dimethoxy silane (donor D) under inert conditions at room temperature. After 10 minutes 5.0 g of the catalyst prepared above (Ti content 1.4 wt.-%) was added and after additionally 20 minutes 5.0 g of vinylcyclohexane (VCH) was added. The temperature was increased to 60° C. during 30 minutes and was kept there for 20 hours. Finally, the temperature was decreased to 20° C. and the concentration of unreacted VCH in the oil/catalyst mixture was analysed and was found to be 200 ppm weight.

Preparation of the catalyst for HECO2b 80 mg of ZN104-catalyst of LyondellBasell is activated for 5 minutes with a mixture of Triethylaluminium (TEAL; solution in hexane 1 mol/1) and Dicyclopentyldimethoxysilane as donor (0.3 mol/l in hexane)—in a molar ratio of 18.7 (Co/ED) after a contact time of 5 min and 10 ml hexane in a catalyst feeder. The molar ratio of TEAL and Ti of catalyst is 220 (Co/TC)). After activation the catalyst is spilled with 250 g propylene into the stirred reactor with a temperature of 23° C. Stirring speed is hold at 250 rpm. After 6 min prepolymersation at 23° C. the polymerisation starts as indicated in table 1.

TABLE 1 Preparation of HECO1, HECO2, HECO2a and HECO2b HECO1 HECO2 HECO2a HECO2b Prepolymer- ization TEAL/Ti [mol/mol] 200 200 220 220 TEAL/donor [mol/mol] 5.01 10 7.3 18 Temperature [° C.] 30 30 30 30 res.time [h] 0.17 0.26 0.08 0.1 Loop Temperature [° C.] 80 76 72 70 Split [%] 34 35 35 32.5 H2/C3 ratio [mol/kmol] 7 25 15 14 C2/C3 ratio [mol/kmol] 0 0 0 0 MFR₂ [g/10 min] 162 160 55 35 XCS [wt.-%] 2.0 2.1 2.0 2.0 C2 content [mol-%] 0 0 0 0.0 GPR 1 Temperature [° C.] 95 80 80 78 Pressure [kPa] 1500 2400 2231 2214 Split [%] 45 40 30 34.5 H2/C3 ratio [mol/kmol] 84 45 150 78 C2/C3 ratio [mol/kmol] 0 0 0 0 MFR₂ [g/10 min] 159 55 55 35 XCS [wt.-%] 2.9 2.0 2.0 2.0 C2 content [mol-%] 0 0 0 0 GPR 2 Temperature [° C.] 85 67 70 71 Pressure [kPa] 1400 2100 2291 2292 Split [%] 21 15 19 21 C2/C3 ratio [mol/kmol] 600 242 584 715 H2/C2 ratio [mol/kmol] 170 23 117 219 MFR₂ [g/10 min] 66 20 11 12 XCS [wt.-%] 20 18 18 19 IV (XCS) [dl/g] 2.9 nd nd nd C2 (XCS) [mol-%] 53 nd nd nd C2 content [mol-%] 18 10 18 12 GPR 3 Temperature [° C.] 67 85 83 Pressure bar 1500 1421 1383 Split [%] 10 16 12 C2/C3 ratio [mol/kmol] 250 585 747 H2/C2 ratio [mol/kmol] 22 93 203 MFR₂ [g/10 min] 5 11 13 XCS [wt.-%] 25 32 30 IV (XCS) [dl/g] 6.3 3.1 2.2 C2 (XCS) [mol-%] 25.7 48 55 C2 content [mol-%] 11.2 19 22 C2 ethylene H2/C3 ratio hydrogen/propylene ratio C2/C3 ratio ethylene/propylene ratio H2/C2 ratio hydrogen/ethylene ratio GPR 1/2/3 1st/2nd/3rd gas phase reactor Loop Loop reactor

A Borstar PP pilot plant comprised of a stirred-tank prepolymerization reactor, a liquid-bulk loop reactor, and three gas phase reactors (GPR1 to GPR3) was used for the main polymerization. The resulting polymer powders were compounded in a co-rotating twin-screw extruder Coperion ZSK 57 at 220° C. with 0.2 wt.-% of Irganox B225 (1:1-blend of Irganox 1010 (Pentaerythrityl-tetrakis(3-(3′,5′-di-tert.butyl-4-hydroxytoluyl)-propionate and tris (2,4-di-t-5 butylphenyl) phosphate) phosphite) of BASF AG, Germany) and 0.05 wt.-% calcium stearate.

Preparation of the Composition (C)

HECO1 and HECO2 (inventive), HECO2a (comparative) or HECO2b (comparative) and optionally PL and HDPE were melt blended on a co-rotating twin screw extruder with 0.1 wt.-% of Songnox 1010FF (Pentaerythrityl-tetrakis(3-(3′,5′-di-tert. butyl-4-hydroxyphenyl)), 0.07 wt.-% Kinox-68 G (Tris (2,4-di-t-butylphenyl) phosphite) from HPL Additives, 0.16 wt % hindered amine light stabilizers which were mixed in a 1:1 blend based on Sabostab UV119 (1,3,5-Triazine-2,4,6-triamine) and Hilite 77(G)(Bis-(2,2,6,6-tetramethyl-4-piperidyl)-sebacate), 0.1 wt % NA11UH (Sodium 2,2′-methylene bis-(4,6-di-tert. butylphenyl) phosphate) and 0.1 wt % Erucamide (13-docosenamide). The polymer melt mixture was discharged and pelletized.

TABLE 2 Properties of comparative and inventive examples collected on 2 mm compact and chemically injection-moulded foamed plates. CE1 CE2 CE3 IE1 IE2 IE3 IE4 HECO1 [wt.-%] 42.5 56.5 56.5 42.5 42.5 56.5 56.5 HECO2 [wt.-%] 26.5 26.5 25.5 25.5 HECO2a [wt.-%] 26.5 25.5 HECO2b [wt.-%] 25.5 PL [wt.-%] 8.0 8.0 8.0 HDPE [wt.-%] 5.0 5.0 5.0 Wollastonite [wt.-%] 14.5 14.5 14.5 14.5 14.5 Talc1 [wt.-%] 14.5 Talc2 [wt.-%] 14.5 Pigments [wt.-%] 1.5 1.5 1.5 1.5 1.5 1.5 1.5 Additives [wt.-%] 2 2 2 2 2 2 2 Properties of compact parts MFR [g/10 min] 28.0 39.0 36.0 21.0 20.0 32.0 27.0 SH in flow sector, 96 h [—] 0.55 0.51 0.54 0.52 0.81 0.64 0.77 SH cross flow sector, 96 h [—] 1.40 1.30 1.4 1.35 1.09 1.56 1.04 SH isotropic sector, 96 h [—] 1.02 1.00 1.00 1.00 1.00 1.15 0.94 Flexural Modulus [MPa] 2157 2613 2663 2272 1886 2678 2505 Charpy impact strength, +23° C. [kJ/m²] 10 5 5 16 14 6 6 Charpy impact strength, −20° C. [kJ/m²] nd 3.6 nd 2.5 nd nd nd Maximum force at break N 1250 1300 1400 1600 1750 1850 Compressive stress at 1 mm MPa 70 75 70 69 80 90 MSEaverage, 1.5 s, G1 [—] 18 7 6 4 3 4 3 MSEmax, 0.8 s, G2 [—] 45 40 40 42 41 45 Properties of foamed parts Cell size [μm] 90 80 70 70 60 60 60 Cell structure [—] coarse coarse coarse fine fine fine fine Part surface [—] poor poor poor good good good good Maximum force at break N nd 900 1000 1200 1300 1400 1650 Compressive stress at 1 mm MPa nd 65 65 69 69 75 75 MSEmax, G2 nd 43 43 41 43 40 43 HECO2a is the commercial heterophasic propylene copolymer EE050AE of Borealis HECO2b is the commercial heterophasic propylene copolymer EE041AE of Borealis PL is the commercial ethylene-octene copolymer Queo8230 of Borealis having a density of 0.880 g/cm³, a melt flow rate MFR₂ (190° C.) of 30.0 g/10 min and an 1-octene content of 7.0 mol-%. HDPE is the commercial high density polyethylene MG9601 of Borealis Wollastonite is the commercial Wollastonite Nyglos 8 of Imerys Talc1 is the commercial Talc Jetfine 3CA of Luzenac Talc2 is the commercial Talc HAR T84 of Luzenac Pigments is a masterbatch of 70 wt.-% of linear density polyethylene (LDPE) and 30 wt.-% carbon black, with MFR (190° C./21.6 kg) of 15 g/10 min. Additives is a masterbatch of Songnox 1010FF (Pentaerythrityl-tetrakis(3-(3′,5′-di-tert. butyl-4-hydroxyphenyl)), Kinox-68 G (Tris (2,4-di-t-butylphenyl) phosphite) from HPL Additives, hindered amine light stabilizers which were mixed in a 1:1 blend based on Sabostab UV119 (1,3,5-Triazine-2,4,6-triamine) and Hilite 77(G)(Bis-(2,2,6,6-tetramethyl-4-piperidyl)-sebacate), NA11UH (Sodium 2,2′-methylene bis-(4,6-di-tert. butylphenyl) phosphate) and Erucamide (13-docosenamide) as outlined above. 

The invention claimed is:
 1. A polypropylene composition (C), comprising: a) a first heterophasic propylene copolymer (HECO1) having a comonomer content of the xylene soluble fraction (XCS) equal or above 40.0 mol %, said first heterophasic propylene copolymer comprising: i) a first matrix being a first propylene polymer (M1) and ii) a first elastomeric propylene copolymer (E1) being dispersed in said first matrix, b) a second heterophasic propylene copolymer (HECO2) having a comonomer content of the xylene soluble fraction (XCS) below 39.0 mol %, wherein the xylene soluble fraction (XCS) of the second heterophasic copolymer (HECO2) has an intrinsic viscosity (IV) above 3.5 dl/g, said second heterophasic propylene copolymer comprising: iii) a second matrix being a second propylene polymer (M2) and iv) a second elastomeric propylene copolymer (E1) being dispersed in said second matrix, c) an inorganic filler (F), d) optionally a high density polyethylene (HDPE), and e) optionally a plastomer (PL) being a copolymer of ethylene and a C₄ to C₈ α-olefin.
 2. The polypropylene composition (C) according to claim 1, comprising: a) 40.0 to 60.0 wt. % of the first heterophasic propylene copolymer (HECO1), b) 21.0 to 31.0 wt. % of the second heterophasic propylene copolymer (HECO2), c) 10.0 to 20.0 wt. % of the inorganic filler (F), d) optionally 2.0 to 10.0 wt. % of the high density polyethylene (HDPE), and e) optionally 5.0 to 15.0 wt. % of the plastomer (PL) being a copolymer of ethylene and a C₄ to C₈ α-olefin, based on the overall polypropylene composition (C).
 3. The polypropylene composition (C) according to claim 1, wherein: i) the matrix of the first heterophasic propylene copolymer (HECO1) being the first propylene polymer (M1) has a melt flow rate MFR₂ (230° C.) determined according to ISO 1133 in the range of 120 to 500 g/10 min and ii) the matrix of the second heterophasic propylene copolymer (HECO2) being the second propylene polymer (M2) has a melt flow rate MFR₂ (230° C.) determined according to ISO 1133 in the range of 40 to 170 g/10 min.
 4. The polypropylene composition (C) according to claim 1, wherein the first heterophasic propylene copolymer (HECO1) has: i) a melt flow rate MFR₂ (230° C.) determined according to ISO 1133 in the range of 50 to 90 g/10 min, and/or ii) a comonomer content in the range of 20.0 to 50.0 mol %, and/or iii) a xylene soluble fraction (XCS) in the range of 10.0 to 35.0 wt. %.
 5. The polypropylene composition (C) according to claim 1, wherein the second heterophasic propylene copolymer (HECO2) has: i) a melt flow rate MFR₂ (230° C.) determined according to ISO 1133 in the range of 1.0 to 15 g/10 min, and/or ii) a comonomer content in the range of 5.0 to 30.0 mol %, and/or iii) a xylene soluble fraction (XCS) in the range of 20.0 to 40.0 wt. %.
 6. The polypropylene composition (C) according to claim 1, wherein the first propylene polymer (M1) and/or the second propylene polymer (M2) are propylene homopolymers.
 7. The polypropylene composition (C) according to claim 1, wherein the first elastomeric propylene copolymer (E1) and/or the second elastomeric propylene copolymer (E2) are copolymers of propylene and ethylene.
 8. The polypropylene composition (C) according to claim 1, having a melt flow rate MFR₂ (230° C.) determined according to ISO 1133 in the range of 10 to 40 g/10 min.
 9. The polypropylene composition (C) according to claim 1, wherein the plastomer (PL) is a copolymer of ethylene and 1-octene.
 10. The polypropylene composition (C) according to claim 1, wherein the inorganic filler (F) is talc and/or wollastonite.
 11. The polypropylene composition (C) according to claim 1, wherein said polypropylene composition (C) is a foamable polypropylene composition.
 12. A foamed article, comprising the polypropylene composition (C) according to claim
 1. 13. The foamed article according to claim 12, wherein said foamed article is an automotive article. 